Synthesis, Structure and Photophysical Properties of Silole-Oxadiazole Copolymers  

作　　者：Tingting Zhang Chaoqiang Zhu Yuwen Ma Chengyun Wang Yongjia Shen 

机构地区：[1]Key Laboratory for Advanced Materials and Institute of Fine Chemicals, East China University of Science and Technology, 130 Meilong Road, Shanghai 200237, China

出　　处：《Chinese Journal of Chemistry》2013年第6期779-786,共8页中国化学（英文版）

基　　金：The authors are grateful to financial support from the National Natural Science Foundation of China，the East China University of Science and Technology

摘　　要：A new conjugated copolymer （PTST-DyOXD） derived from 1,1-dimethyl-3,4-diphenyl-2,5-bis（5-bromo-2- thienyl）-silole （TST） and 2,5-bis（4-ethynylphenyl）-l,3,4-oxadiazole （DyOXD） was synthesized by Pd（0）-catalyzed Sonogashira coupling reaction. For comparison, another copolymer without acetenyl group （PTST-OXD） was also synthesized by Pd（0）-catalyzed Suzuki coupling reaction. Chemical structures and optoelectronic properties of the copolymers were characterized by IH NMR, 13C NMR, IR, UV-vis absorption, photoluminescence and cyclic voltammetry. The number-average molecular weight （Mn） is 4010 Da for PTST-DyOXD and 3890 Da for PTST-OXD, respectively. The thermogravimetric analysis （TGA） measurements show that they have good thermal stability with decomposition temperature at 312 and 318 ~C, respectively. The optical band gap is 2.21 eV for PTST-DyOXD and 2.10 eV for PTST-OXD based on the absorption onset. CV analysis revealed the LUMO level of PTST-DyOXD is -3.04 eV, lower than that of PTST-OXD （about -2.89 eV）, which is attributed to the introduction of acetylene group in PTST-DyOXD, increasing the system of the conjugate chain length.A new conjugated copolymer （PTST-DyOXD） derived from 1,1-dimethyl-3,4-diphenyl-2,5-bis（5-bromo-2- thienyl）-silole （TST） and 2,5-bis（4-ethynylphenyl）-l,3,4-oxadiazole （DyOXD） was synthesized by Pd（0）-catalyzed Sonogashira coupling reaction. For comparison, another copolymer without acetenyl group （PTST-OXD） was also synthesized by Pd（0）-catalyzed Suzuki coupling reaction. Chemical structures and optoelectronic properties of the copolymers were characterized by IH NMR, 13C NMR, IR, UV-vis absorption, photoluminescence and cyclic voltammetry. The number-average molecular weight （Mn） is 4010 Da for PTST-DyOXD and 3890 Da for PTST-OXD, respectively. The thermogravimetric analysis （TGA） measurements show that they have good thermal stability with decomposition temperature at 312 and 318 ~C, respectively. The optical band gap is 2.21 eV for PTST-DyOXD and 2.10 eV for PTST-OXD based on the absorption onset. CV analysis revealed the LUMO level of PTST-DyOXD is -3.04 eV, lower than that of PTST-OXD （about -2.89 eV）, which is attributed to the introduction of acetylene group in PTST-DyOXD, increasing the system of the conjugate chain length.

关 键 词：2 5-bis（5-bromo-2-thienyl）silole 2 5-bis（4-ethynylphenyl）-1 3 4-oxadiazole Sonogashira reaction Suzuki reaction conjugated polymer 

分 类 号：O632.13[理学—高分子化学] TB333[理学—化学]