用于稠化胶体的高吸水树脂的制备及吸水性能研究  

Study on preparation and properties of super absorbent resin thickening agent of thickening colloid

作　　者：黄艳芹[1] 

机构地区：[1]新乡学院化学与化工学院,河南新乡453003

出　　处：《功能材料》2013年第14期2006-2009,共4页Journal of Functional Materials

基　　金：国家自然科学基金资助项目(11074066);河南省基础与前沿技术研究计划资助项目(122300410431)

摘　　要：以丙烯酸和丙烯酰胺为单体,N,N-亚甲基双丙烯酰胺为交联剂,过硫酸钾为引发剂,采用水溶液聚合法制备了高吸水树脂。通过正交实验法研究了单体浓度、丙烯酸中和度、引发剂用量和交联剂用量对树脂吸水倍率的影响。最终获得了在蒸馏水中吸水倍率高达3114g/g,在质量分数0.9%NaCl溶液中吸水倍率达157g/g的高吸水树脂,该树脂能够用作稠化胶体的稠化剂来提高胶体的实用性能。The super absorbent resin was prepared by the polymerization of aqueous solution.The copolymerization was carried out using acrylic acid and acrylamide as monomer,N,N-methylene bisacrylamide as crosslinking agent and potassium persulfate as initiator.The effects of monomer concentration,the degree of acrylic acid,initiator dosage and crosslinker dosage on water absorbency were investigated by orthogonal test.The super absorbent resin was obtained,its water absorbency was 3114g/g in distilled water and 157g/g in 0.9wt% NaCl solution.It could be used as thickening agent to improve the thickening colloid practical performance.

关 键 词：稠化胶体 高吸水树脂 吸水倍率 

分 类 号：TD75[矿业工程—矿井通风与安全]