MnO_2和Co_2Y联合添加对Ni-Zn铁氧体磁损耗的影响  

Influence of MnO_2 and Co_2Y doping on the power loss of Ni-Zn ferrites

作　　者：马睿[1] 张夜雨[1] 王庆莉[1] 陆公道[1] 冯双久[1] 刘先松[1] 

机构地区：[1]安徽大学物理与材料科学学院磁性材料安徽省工程技术研究中心,安徽合肥230039

出　　处：《磁性材料及器件》2013年第4期58-60,共3页Journal of Magnetic Materials and Devices

摘　　要：采用传统陶瓷工艺制备了MnO2和Co2Y联合添加的Ni0.8Zn0.2Fe2O4铁氧体材料,研究了材料的结构与功耗。结果表明,随着MnO2添加量的增多,Ni-Zn铁氧体的损耗经历增大-减小-增大的变化,最佳添加量为1.2wt%。进一步研究表明,与不添加MnO2的材料相比,最佳添加时铁氧体的磁滞损耗系数与涡流损耗系数都减小,但剩余损耗系数有所增大。MnO2 and Co2Y doped Ni0.8Zn0.2Fe2O4 ferrites were prepared by traditional ceramic process, the structure and power loss of the ferrites were investigated. It was found that the power loss increases first, then decreases and increases again with increasing MnO2 doping, and the optimal MnO2 doping was 1.2wt%. Compared with sample without MnO2 doping, further investigation revealed that the sample with 1.2wt% MnO2 doping has lower hysteresis and eddy current loss coefficient but higher residual loss coefficient.

关 键 词：NI-ZN铁氧体 MnO2掺杂 损耗 

分 类 号：TM277.1[一般工业技术—材料科学与工程]