Effect of Niobium on Dynamic Recrystallization Behavior of 5%Ni Steel  

作　　者：LEI Xiao-rong DING Qing-feng CHEN Yuan-yuan RUI Xiao-long LI Shu-rui WANG Qing-feng 

机构地区：[1]State Key Laboratory of Metastable Materials Science and Technology, Yanshan University [2]Research and Development Center, Wuhan Iron and Steel Company

出　　处：《Journal of Iron and Steel Research International》2013年第6期38-44,共7页

基　　金：Item Sponsored by National High Technology Research and Development Program of China ( 2007AA03Z506 )

摘　　要：The single-pass hot compressions of two 5%Ni steels with and without niobium addition at different temperatures of 800-1 150℃and strain rates of 0.01-1s-1 were performed by using a Gleeble-3500 thermal simulator and the effect of niobium on the dynamic recrystallization （ DRX ） behavior was analyzed.The results showed that the niobium addition of 0.04% can retard DRX in 5%Ni steel significantly by increasing the activation energy for DRX from 394 to 462kJ / mol.The critical strain required for starting DRX in 5%Ni steel was increased by 0.04-0.10 with niobium addition when the steel was deformed at a strain rate of 0.01s-1 and temperatures varied from 950 to 1 000℃.The critical temperature required for starting DRX in 5%Ni steel was also increased from 1 000 to 1 050℃ with niobium addition when the steel was deformed at a strain rate of 0.1s-1 .Such a retarded DRX occurring in Nb-added 5%Ni steel can be attributed to the pinning effect of precipitates containing niobium.The single-pass hot compressions of two 5%Ni steels with and without niobium addition at different temperatures of 800-1 150℃and strain rates of 0.01-1s-1 were performed by using a Gleeble-3500 thermal simulator and the effect of niobium on the dynamic recrystallization （ DRX ） behavior was analyzed.The results showed that the niobium addition of 0.04% can retard DRX in 5%Ni steel significantly by increasing the activation energy for DRX from 394 to 462kJ / mol.The critical strain required for starting DRX in 5%Ni steel was increased by 0.04-0.10 with niobium addition when the steel was deformed at a strain rate of 0.01s-1 and temperatures varied from 950 to 1 000℃.The critical temperature required for starting DRX in 5%Ni steel was also increased from 1 000 to 1 050℃ with niobium addition when the steel was deformed at a strain rate of 0.1s-1 .Such a retarded DRX occurring in Nb-added 5%Ni steel can be attributed to the pinning effect of precipitates containing niobium.

关 键 词：5%Ni steel dynamic recrystallization NIOBIUM PRECIPITATION pinning effect 

分 类 号：TG142.15[一般工业技术—材料科学与工程]