锂离子电池用层状LiMnO_2的合成及性能  

Synthesis and electrochemical behavior of layered LiMnO_2

作　　者：关昶[1] 穆庆峰[2] 刘伶[1] 

机构地区：[1]吉林化工学院化工与材料工程学院,吉林吉林132022 [2]中国石油吉林石化公司,吉林吉林132022

出　　处：《吉林化工学院学报》2013年第7期15-18,共4页Journal of Jilin Institute of Chemical Technology

摘　　要：采用离子交换法合成了准确化学计量比的层状LiMnO2锂离子电池正极材料.通过热重分析确定了前驱体NaMnO2的焙烧温度为800℃,通过XRD测试确定了前躯体的焙烧时间为48 h.采用电子扫描电镜测试LiMnO2材料的颗粒平均粒径为3μm.在2.0～4.5 V(vs Li/Li+)条件下进行充放电测试,结果表明LiMnO2经过50次循环后,放电比容量仍可达到125 mAh/g(0.2 C).Stoichiometric layered LiMnO2 cathode material was successfully synthesized by ion-exchange method.Thermogravimetry（TG） and X-Ray Diffraction（XRD） revealed that the layered NaMnO2 can be synthesized at 800 ℃ for 48 h.Scanning Electron Microscope（SEM） observations showed that the particle size of synthesized LiMnO2 was about 3 μm.Galvanostatic charge-discharge tests between 2.0 and 4.5 V（vs Li/Li＋） confirmed the LiMnO2 electrode had good electrochemical properties.The discharge capacity was about 125 mAh·g-1 even after 50 cycles.

关 键 词：锂离子电池 正极材料 层状LIMNO2 离子交换法 

分 类 号：TM912[电气工程—电力电子与电力传动]