Study on typical hole defects in AZ91D magnesium alloy prepared by low pressure lost foam casting  

作　　者：Li Jiqiang Zhao zhong Fan Zitian Dong Xuanpu Shi Hualiang 

机构地区：[1]School of Mechanical and Energy, Ningbo Institute of Technology,Zhejiang University [2]Ningbo University of Technology [3]State Key Laboratory of Material Processing and Die & Mould Technology,Huazhong University of Science and Technology

出　　处：《China Foundry》2013年第4期232-236,共5页中国铸造（英文版）

基　　金：financially supported by the National High Technology Research and Development Program of China(Project No.2007AA03Z113);the Zhejiang Province Natural Science Foundation of China(Project Nos.LY12E05015 and Y1110106)

摘　　要：The hole defects can easily occur in magnesium alloy castings that are prepared by low pressure lost foam casting(LP-LFC)process when the process parameters such as vacuum,pouring temperature and f illing velocity are not properly selected.In this study,the forming mechanism of the hole defects in AZ91D magnesium castings by LP-LFC process was investigated.The shape,location and surface appearance of the hole defects were observed using optical microscopy and scanning electron microscopy,and the chemical composition on the surface of the holes was analyzed using energy spectrometer.The result indicates that there are two types of hole defects,i.e.,the pyrolysis products related hole defects,including concentrative hole and blow hole defects,and slag related hole defects.The concentrative hole and the blow-hole defects were formed either by the liquidEPS degradation products entrapped in the molten metal under the condition that the pouring temperature is equal to or lower than 730℃,or by the hindered transport of EPS pyrolysis products.Some irregular shape hole defects were caused by slag or by coating slough entrapment when the pouring temperature is equal to 750℃and the f illing velocity is equal to or greater than 100 mm·s-1.To reduce or eliminate the hole defects,the vacuum and f illing velocity must be properly chosen to ensure that the metal front prof ile exhibits convex shape and in laminar current state,and the pouring temperature should be just high enough to ensure that the molten melt has adequate heat energy to complete the foam pyrolysis and to fully occupy the mould.For AZ91D magnesium castings in this study,the parameters should be 730℃pouring temperature,0.02-0.03 MPa vacuum and 80mm·s-1f illing velocity.The hole defects can easily occur in magnesium alloy castings that are prepared by low pressure lost foam casting （LP-LFC） process when the process parameters such as vacuum, pouring temperature and filling velocity are not properly selected. In this study, the forming mechanism of the hole defects in AZ91D magnesium castings by LP-LFC process was investigated. The shape, location and surface appearance of the hole defects were observed using optical microscopy and scanning electron microscopy, and the chemical composition on the surface of the holes was analyzed using energy spectrometer. The result indicates that there are two types of hole defects, i.e., the pyrolysis products related hole defects, including concentrative hole and blow hole defects, and slag related hole defects. The concentrative hole and the blow-hole defects were formed either by the liquid- EPS degradation products entrapped in the molten metal under the condition that the pouring temperature is equal to or lower than 730 ℃, or by the hindered transport of EPS pyrolysis products. Some irregular shape hole defects were caused by slag or by coating slough entrapment when the pouring temperature is equal to 750 ℃ and the filling velocity is equal to or greater than 100 mm.s-1. To reduce or eliminate the hole defects, the vacuum and filling velocity must be properly chosen to ensure that the metal front profile exhibits convex shape and in laminar current state, and the pouring temperature should be just high enough to ensure that the molten melt has adequate heat energy to complete the foam pyrolysis and to fully occupy the mould. For AZ91D magnesium castings in this study, the parameters should be 730 ℃ pouring temperature, 0.02-0.03 MPa vacuum and 80 mm.s^-1 filling velocity.

关 键 词：magnesium alloy low-pressure lost foam casting hole defects 

分 类 号：TG146.22[一般工业技术—材料科学与工程] TG249.6[金属学及工艺—金属材料]