Influence of chromium modification on the properties of MnO_x-FeO_x catalysts for the low-temperature selective catalytic reduction of NO by NH_3  

作　　者：Kai Shen Yaping Zhang Xiaolei Wang Haitao Xu Keqin Sun Changcheng Zhou 

机构地区：[1]Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education,School of Energy and Environment,Southeast University

出　　处：《Journal of Energy Chemistry》2013年第4期617-623,共7页能源化学（英文版）

基　　金：supported by Jiangsu Natural Science Foundation (No. BK2012347);the National High Technology and Development Program of China (863 Programs, No.2007AA061802)

摘　　要：Catalytic properties of MnOx-FeOx complex oxide （hereafter denoted as Mn-Fe） catalysts modified with different loadings of chromium oxide were investigated by using the combination of physico-cbemical techniques, such as N2 physisorption, X-ray diffraction （XRD）, high-resolution transmission electron microscope （HRTEM）, in situ Fourier transform infrared spectroscopy （in situ FT-IR） and temperature-programmed reduction （TPR） and their catalytic activities were evaluated with the selective catalytic reduction （SCR） of NOx by NH3. It was found that with the addition of Cr, more NO could be removed in the low-temperature window （below 120 ℃）. Among the tested catalysts, Mn-Fe- Cr （2 ： 2 ： 1） catalyst exhibited the best catalytic performance at 80 ℃ with the NO conversion higher than 90%. The combination of the reaction and characterization results indicated that （1） the strong interaction among tertiary metal oxides existed in the catalysts when Cr was appropriately added, which made the active components better dispersed with less agglomeration and sintering and the largest BET specific surface area could be obtained; （2） Cr improved the low-temperature reducibility of the catalyst and promoted the formation of the active intermediate （-NH3＋）, which favored the low-temperature SCR reaction.Catalytic properties of MnOx-FeOx complex oxide （hereafter denoted as Mn-Fe） catalysts modified with different loadings of chromium oxide were investigated by using the combination of physico-cbemical techniques, such as N2 physisorption, X-ray diffraction （XRD）, high-resolution transmission electron microscope （HRTEM）, in situ Fourier transform infrared spectroscopy （in situ FT-IR） and temperature-programmed reduction （TPR） and their catalytic activities were evaluated with the selective catalytic reduction （SCR） of NOx by NH3. It was found that with the addition of Cr, more NO could be removed in the low-temperature window （below 120 ℃）. Among the tested catalysts, Mn-Fe- Cr （2 ： 2 ： 1） catalyst exhibited the best catalytic performance at 80 ℃ with the NO conversion higher than 90%. The combination of the reaction and characterization results indicated that （1） the strong interaction among tertiary metal oxides existed in the catalysts when Cr was appropriately added, which made the active components better dispersed with less agglomeration and sintering and the largest BET specific surface area could be obtained; （2） Cr improved the low-temperature reducibility of the catalyst and promoted the formation of the active intermediate （-NH3＋）, which favored the low-temperature SCR reaction.

关 键 词：MnOx-FeOx Cr MODIFICATION low-temperature selective catalytic reduction CATALYSTS 

分 类 号：X701[环境科学与工程—环境工程] O643.32[理学—物理化学]