PVDF中空纤维膜的制备及冷拉伸处理对其性能的影响  

Preparation of PVDF Hollow Fiber Membrane and the Effect of Cool Stretching Process on Its Properties

作　　者：张秋吉[1] 刘波[1] 沈鹏[2] 张玉坤[3] 杨昌玉[2] 

机构地区：[1]深圳大学化学与化工学院,广东深圳518060 [2]广州中国科学院先进技术研究所水科学研究中心,广东广州511458 [3]华南理工大学机械与汽车工程学院,广东广州510640

出　　处：《塑料工业》2013年第S01期81-85,共5页China Plastics Industry

摘　　要：用干-湿纺丝法制备聚偏氟乙烯（PVDF）中空纤维膜，用万能拉力仪进行冷拉伸处理，分别拉伸0．9、1．2、1．5、1．8倍。研究拉伸前后的中空纤维膜的纯水通量、牛血清白蛋白（BSA）通量衰减、孔隙率等基本性能，用电镜观察膜的表面形貌，用万能拉力仪测试膜的力学性能，用红外光谱仪分析膜内的晶体结构。结果显示，拉伸会影响中空纤维膜的基本性能及表面形貌。拉伸1．8倍为最佳拉伸倍数，此法可简易制得性能良好的高通量微孔膜。In this paper, PVDF hollow fiber microfiltration membrane was prepared with dry-wet spinning technique. Then the PVDF hollow fiber mierofiltration membrane was treated with stretching process, stretch ratio was O. 9, 1.2, 1.5, 1.8, respectively. The effect of stretching process on the basic properties such as water flux, rejection rate and porosity were discussed. Scanning electron microscopy （SEM） and tensile testing machine were Used to characterize the morphological changes and mechanical properties. By means of attenuated total reflection-Fourier transform infrared spectroscopy, the crystal structures were discussed. The results indicated the best stretching ratio was 1.8 times. This kind of technique could be used to prepare high flux PVDF hollow fiber microfiltration membrane expediently.

关 键 词：聚偏氟乙烯 中空纤维膜 拉伸 高通量 

分 类 号：TQ051.893[化学工程] TQ340.64