常温铁系耐蚀磷化液的研制和应用  

The Development and Application of Room Temperature Corrosion Resistant Phosphating Solution for Iron Series

作　　者：孟德军[1] 滕培棠[2] 

机构地区：[1]中国邮电工业总公司明水邮电通信设备厂,山东济南250200 [2]山东汽车总公司明水汽车配件厂,山东济南250200

出　　处：《电镀与精饰》2000年第5期14-16,共3页Plating & Finishing

摘　　要：分别对铁系耐蚀磷化液和 MT- 1 2 6添加剂的配方、配制、性能作了介绍。研制的 MT- 1 2 6含量达到 4 0 m L/ L时 ,磷化膜性能最佳。实验表明 :最佳磷化液中形成的膜层 Cu SO4点滴 >30 s,Na Cl浸泡 >6h,室内挂片 90天无明显锈蚀。Formulas, making up procedure and properties of the developed Fe series room temperature corrosion resistant phosphating solution and the MT 126 additive were introduced. When the MT 126 was up to 40 mL/L in the phosphating solution, the phosphating film had the optimum properties. The experimental results showed that the film obtained in the optimum phosphating solution could be withstand CuSO 4 corrosion test more than 30 s and NaCl immersion test more than 6 h and the specimen was no obvious rust after hanging indoor for 90 days.

关 键 词：铁系 磷化液 耐蚀 MT-126添加剂 金属 表面处理 

分 类 号：TG174.445[金属学及工艺—金属表面处理]