Al-6.6Si铝合金MSMT法流变压铸成型研究  被引量:2

Experimental Studies on Processing of Al-6.6Si Alloy prepared by MSMT Rheocasting

在线阅读下载全文

作  者:梁博[1] 王亚宝[1] 刘建朝[1] 张志峰[1] 徐骏[1] 

机构地区:[1]北京有色金属研究总院国家有色金属复合材料工程技术研究中心,北京100088

出  处:《铸造技术》2013年第9期1174-1176,共3页Foundry Technology

摘  要:将自行设计的分散混合法流变制浆技术与压铸技术相结合,对Al-6.6Si铝合金进行流变压铸成型试验。结果表明:半固态流变压铸工艺与传统液态斥铸工艺有很大不同,在压射压力40MPa,压射速度2.0m/s,压射室和模具预热温度200℃,半固态浆料温度控制在610~615℃时,可以得到充型完好、组织均匀的水泵盖压铸件,压铸件的抗托强度和断后伸长率分别比液态压铸提高15%和50%。Combining the MSMT method with die-casting, the rhecasting forming process for A1-6.6Si aluminum alloy was investigated. The results show that there is a great difference between semisolid rhecasting and traditional die-casting, the pump lid parts with well filled shape and uniform microstructures can be achieved with injection pressure of 40 MPa, injection speed of 2.0 m/s, injection chamber and mould temperature of 200 ℃, semisolid slurry temperature of 610-615 ℃, and the tensile strength and elongation of the pump lid parts is increased by 15% and 50%, respectively compared with the liquid casing ones.

关 键 词:分散混合法流变制浆技术(MSMT法) 压射压力 压射速度 

分 类 号:TG249.2[金属学及工艺—铸造]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象