铸坯角部皮下裂纹的演变规律研究  

Mechanism and Control of Subsurface Crack in Slab Corner

作　　者：李金波[1] 路殿华[1] 李建文[1] 

机构地区：[1]河北钢铁集团邯钢技术中心,河北邯郸056015

出　　处：《中国冶金》2013年第9期26-30,59,共6页China Metallurgy

摘　　要：热轧卷板上出现的不同于常规发纹的短直形边部直裂纹缺陷对产品的影响较大。轧钢环节的中间坯显示铸坯清角部位出现规则性斜向裂纹，通过使用电镜、金相、酸洗等检测方法对卷板、中间坯、连铸坯进行检测分析其形成机制，研究铸坯角部皮下10～30mm范围内的裂纹演变规律，对解决卷板成品边部缺陷提出指导。The straight crack at short straight edge on the hot-rolled coil is a great impact on the product. It differs from conventional crack pattern. The middle diagonal cracks appear in blank. Slab, blank and coil were analyzed with electron microscopy, metallography, pickling and other detection methods to detect the formation mechanism. The surface edge quality of coil was improved to prevent the generation of such defect.

关 键 词：直形裂纹 铸坯皮下裂纹 中间坯 卷板 

分 类 号：TG245[金属学及工艺—铸造]