端羟基聚环氧氯丙烷的合成与表征  

Synthesis and Characterization of Hydroxyl-Terminated Polyepichlorohydrin

作　　者：周立民[1] 高政[1] 

机构地区：[1]武汉工程大学材料科学与工程学院,湖北武汉430073

出　　处：《化学推进剂与高分子材料》2013年第5期46-49,共4页Chemical Propellants & Polymeric Materials

摘　　要：以3–三氟氧硼–1–氯–2–丙氧基三苯基磷为引发剂,四氢呋喃为溶剂,三氟化硼为催化剂,进行环氧氯丙烷阳离子开环聚合,合成了黏均相对分子质量较高的端羟基聚环氧氯丙烷(PECH),探讨了起始剂和催化剂的比例、聚合反应温度和时间对产物的影响。结果表明,引发剂、催化剂与单体的摩尔比为1∶1∶200,在0℃下反应23 h,PECH收率大于90%。The hydroxyl-terminated polyepichlorohydrin （PECH） with higher viscosity average relative molecular mass was synthesized by cationic ring-opening polymerization of epichlorohydrin using 3-boron trifluoride oxide-1- chloro-2-propanoxy triphenyl phosphonium as initiator, tetrahydrofuran as solvent and boron trifluoride as catalyst. The influence of initiator and catalyst ratio, polymerization reaction temperature and time on product was discussed. The results show that the yield of PECH is more than 90% at 0 ℃ for 23 h reaction when n（initiator） ： n（catalyst） ： n（mono- mer）= 1 ： 1 ： 200.

关 键 词：聚环氧氯丙烷 开环聚合反应 3-三氟氧硼-1-氯2-丙氧基三苯基磷 

分 类 号：TQ436[化学工程]