裂纹长度对提升机主轴断裂参量的影响分析  

Effect of Crack Length on Fracture Parameters of an Elevator Shaft

作　　者：赵凌燕[1] 薛河[2] 焦康[2] 唐伟[2] 

机构地区：[1]西安科技大学理学院,西安710054 [2]西安科技大学机械工程学院,西安710054

出　　处：《煤矿机械》2013年第9期110-112,共3页Coal Mine Machinery

基　　金：陕西省教育厅科研计划项目(11JK0883);西安科技大学科研培育基金项目(201138)

摘　　要：针对最危险的一种工况,模拟计算了提升机主轴高应力区半椭圆形表面裂纹附近的应力应变场,分析了不同裂纹长度时主轴各断裂参量的变化规律。研究结果表明,裂纹中心点处的应力和J积分比较小,而应变比较大。裂纹扩展最快的部位并不是裂纹最深处。在相同载荷条件下,裂纹越长,裂纹扩展驱动力越大,裂纹越容易扩展。In the high stress range of an elevator shaft, the stress-strain field ahead of a semi- elliptical surface crack is simulated under the most dangerous loading conditions. And the variations of fracture parameters in the elevator shaft crack front are analyzed when the crack length changes. The result shows that the stress and J-integral at the crack center point are small while the strain is relatively large. The fastest growing part is not the crack deepest part. Under the same loading conditions, longer the crack length is, greater the crack driving force is, and the crack is more susceptible to propagate.

关 键 词：提升机主轴 裂纹长度 断裂参量 驱动力 

分 类 号：TD53[矿业工程—矿山机电]