NaA分子筛膜的制备及其渗透蒸发性能  

Preparation and Pervaporation Performance of NaA Zeolite Membranes

作　　者：鲜建[1,2] 彭东 吕高孟[1] 雷骞[1] 张小明[1] 

机构地区：[1]中国科学院成都有机化学研究所,四川成都610041 [2]中国科学院大学,北京100049 [3]西安向阳航天材料股份有限公司天华化工事业部,陕西西安710025

出　　处：《合成化学》2013年第5期596-599,共4页Chinese Journal of Synthetic Chemistry

摘　　要：采用喷涂法在多孔α-Al2O3载体上制备了NaA分子筛膜(M),其结构和形貌经SEM和XRD表征。对M的渗透蒸发性能进行了研究,结果表明:喷涂时间和晶种浓度是影响M渗透蒸发性能的关键因素。在喷涂时间为30 s,晶种浓度为1 wt%的最佳条件下制备的M,在348 K时对90 wt%乙醇的渗透通量为2.64kg·m-2·h-1,分离因子>10 000。A spraying-seeding method has been developed to prepare NaA zeolite membranes（M） on porous α-Al2O3 tubes.The structures and morphologies of M were characterized by SEM and XRD.The pervaporation properties of M were investigated.The results showed that the spraying time and seed concentration were the crucial factors for the pervaporation properties of M.Permeation flux of M is 2.64 kg · m-2 · h-1 and separation factor is ＞ 10 000 for separating 90 wt％ ethanol under optimum conditions[seed concentration was 1 wt％ and spraying time was 30 s at 348 K] obtaining M.

关 键 词：NAA分子筛膜 喷涂法 制备 渗透蒸发性能 

分 类 号：TQ028.8[化学工程]