Capture of carbon dioxide from flue gas on TEPA-grafted metal-organic framework Mg_2 (dobdc)  

作　　者：Yan Cao Fujiao Song Yunxia Zhao Qin Zhong 

机构地区：[1]School of Chemical Engineering, Nanjing University of Science and Technology [2]School of Environmental Science and Engineering, Yancheng Institute of Technology

出　　处：《Journal of Environmental Sciences》2013年第10期2081-2087,共7页环境科学学报（英文版）

摘　　要：Carbon dioxide （CO2） adsorption on a standard metal-organic framework Mg2（dobdc） （Mg/DOBDC or Mg-MOF-74） and a tetraethylenepentamine （TEPA） modified Mgz（dobdc） （TEPA-Mg/DOBDC） were investigated and compared. The structural information, surface chemistry and thermal behavior of the adsorbent samples were characterized by X-ray powder diffraction （XRD）, infrared spectroscopy （IR）, thermogravimetric analysis （TGA） and nitrogen adsorption-desorption isotherm analysis. CO2 adsorption capacity was measured by dynamic adsorption experiments with N2-CO2 mixed gases at 60℃. Results showed that the CO2 adsorption capacity of Mg/DOBDC was significantly improved after amine modification, with an increase from 2.67 to 6.06 mmol CO2/g adsorbent. Moreover, CO2 adsorption on the TEPA-Mg/DOBDC adsorbent was promoted by water vapor, and the adsorption capacity was enhanced to 8.31 mmol CO2/g absorbent. The adsorption capacity of the TEPA-Mg/DOBDC adsorbent dropped only 3% after 5 consecutive adsorption]desorption cycles. Therefore, this kind of adsorbent can be considered as a promising material for the capture of CO2 from flue gas.Carbon dioxide （CO2） adsorption on a standard metal-organic framework Mg2（dobdc） （Mg/DOBDC or Mg-MOF-74） and a tetraethylenepentamine （TEPA） modified Mgz（dobdc） （TEPA-Mg/DOBDC） were investigated and compared. The structural information, surface chemistry and thermal behavior of the adsorbent samples were characterized by X-ray powder diffraction （XRD）, infrared spectroscopy （IR）, thermogravimetric analysis （TGA） and nitrogen adsorption-desorption isotherm analysis. CO2 adsorption capacity was measured by dynamic adsorption experiments with N2-CO2 mixed gases at 60℃. Results showed that the CO2 adsorption capacity of Mg/DOBDC was significantly improved after amine modification, with an increase from 2.67 to 6.06 mmol CO2/g adsorbent. Moreover, CO2 adsorption on the TEPA-Mg/DOBDC adsorbent was promoted by water vapor, and the adsorption capacity was enhanced to 8.31 mmol CO2/g absorbent. The adsorption capacity of the TEPA-Mg/DOBDC adsorbent dropped only 3% after 5 consecutive adsorption]desorption cycles. Therefore, this kind of adsorbent can be considered as a promising material for the capture of CO2 from flue gas.

关 键 词：metal-organic framework amine modification carbon dioxide adsorption 

分 类 号：X511[环境科学与工程—环境工程]