防老剂对HTPB-IPDI高燃速推进剂性能影响研究(Ⅱ)  

Effect of Antioxidant on Properties of High Burning Rate HTPB-IPDI Propellant(Ⅱ)

作　　者：鲁国林[1] 刘学[1] 

机构地区：[1]中国航天科技集团公司四院四十二所,湖北襄樊441003

出　　处：《固体火箭技术》2000年第3期34-36,共3页Journal of Solid Rocket Technology

摘　　要：采用高温加速老化方法 ,研究了胺类防老剂 H(N,N′-二苯基对苯二胺 )和酚类防老剂甲叉 44 2 6 -S(硫代双 -3,5 -二叔丁基 -4 -羟苄基 )对 HTPB/ IPDI高燃速推进剂贮存性能的影响。实验结果表明 ,随着贮存时间的延长 ,推进剂的常温抗拉强度升高 ,常温、高温、低温下的伸长率降低 ,加入甲叉 44 2 6 -S的 HTPB/ IPDI推进剂的高温贮存性能优于防老剂 H。By accelerated aging tests at high temperature,the effect of antioxidant H(N,N′-diphenyl-p-phenylene diamine)and 4426-S(thio-bis-3,5-di-tert-butyl-4-hydroxylbenzyl))on mechanical properties of HTPB/IPDI propellants with high burning rate was studied.The results show that tensile strengh of propellant at 25℃ increases and elongation decreases at 25℃、70℃、-40℃ with extension of the storage time.The accelerated aging storage property of HTPB/IPDI propellant with the addition of antioxidant 4426-S is superior to antioxidant H.

关 键 词：可储存性 HTPB/IPDI推进剂 防老剂 丁羟推进剂 

分 类 号：V512.3[航空宇航科学与技术—航空宇航推进理论与工程]