硬质合金激光-TIG复合焊焊缝成形及缺陷分析  

Analysis on Welding Defects and Weld Formation of Cemented Carbide Laser-TIG Welds

作　　者：马丁[1] 于治水[1] 曹晓莲[1] 徐培全[1] 

机构地区：[1]上海工程技术大学材料工程学院,上海201620

出　　处：《热加工工艺》2013年第19期144-147,共4页Hot Working Technology

基　　金：国家自然科学基金项目(51105240);上海工程技术大学研究生科研创新课题项目(13KY0503)

摘　　要：针对硬质合金焊接过程中容易出现的未熔透、气孔以及裂纹等缺陷,以硬质合金与因瓦合金的焊接为研究对象,分析了在其激光-TIG复合焊过程中焊缝成形、气孔和裂纹的形成原因及其影响因素,初步讨论了硬质合金激光-TIG焊接过程的缺陷及其分布位置特征。With the development of powder metallurgy and welding technique, cemented carbide was widely used in different applications. Moreover, the ratio increases sharply. According to such welding defects as non-penetration, gas porosity and cracks, the welded joints between cemented carbide and invar alloy were investigated using laser-TIG （tungsten inert gas） hybrid welding. The reasons and influencing factors on the weld formation, gas porosity and cracks were analyzed followed by discussion on the characterization of welding defects and distribution.

关 键 词：硬质合金 激光 TIG复合焊 气孔 裂纹 

分 类 号：TG456.7[金属学及工艺—焊接]