“刚性防水和混凝土结构自防水”系列报道之十四 表面防水混凝土在荷载作用下的渗透性试验研究  

Study on Permeability of Concrete Coated with Silicone Waterproofing Agent under Load

作　　者：马志鸣 李丹 刘晓东 黄巍林[2] 

机构地区：[1]青岛市市政工程设计研究院有限责任公司,山东青岛266100 [2]青岛酒店管理职业技术学院酒店工程学院,山东青岛266100

出　　处：《中国建筑防水》2013年第20期1-3,7,共4页China Building Waterproofing

摘　　要：对硅烷表面防水混凝土试件进行了弯曲试验,测定在不同应力作用下试件的抗水渗透性和抗氯离子渗透性。结果表明,试件的抗水渗透性、抗氯离子渗透性均随着作用应力的提高而降低,但是在不同应力作用下,硅烷表面防水试件较空白试件具有更好的抗渗透性。文章指出,对混凝土结构进行硅烷表面防水处理可以提高其耐久性并延长使用寿命。Resistances to water and chloride ion penetration of concrete samples coated with silicone waterproofing agent under different bend stresses are tested. The results show that the resistances to water and chloride ion penetration of samples reduces with the increasing of bend stress, but samples coated with silicone waterproofing agent have better impermeability than blank samples under different stresses. The article points out that concrete structures coated with silicone waterproofing agent will have better durability and longer service life.

关 键 词：混凝土试件 硅烷表面防水处理 渗透性能 弯曲试验 耐久性能 

分 类 号：TU502[建筑科学—建筑技术科学] TU528.32