聚氨酯用丁二酸聚酯二醇的合成  

The Synthesis of Succinic Acid Polyester Diol for Polyurethane

作　　者：俞中锋[1] 李斌[2] 姚成[1] 

机构地区：[1]南京工业大学理学院,南京210009 [2]西南科技大学材料科学与工程学院,四川绵阳621000

出　　处：《聚氨酯工业》2013年第5期12-15,共4页Polyurethane Industry

摘　　要：研究了以丁二酸、乙二醇为主要原料制备聚氨酯用丁二酸聚酯二醇的方法,考察了原料酸醇比、反应温度、催化剂种类及用量、反应时间等对反应的影响。结果表明,当丁二酸与乙二醇摩尔比为1∶1.8、催化剂为辛酸亚锡、用量为原料总质量的0.3%、预酯化反应温度为180℃、减压缩聚温度为160℃、时间为5 h、真空度1.99 kPa时,酯化率达到99%,产品羟值为105 mgKOH/g,酸值为0.91 mgKOH/g。The synthesis of succinic acid polyester diol for polyurethane was researched using succinic acid （SA） and ethylene glycol（EG） as the main raw materials. The effects of molar ration of SA and EG, reaction tem- perature, types and concentration of catalyst, reaction time on esterification ration were investigated. The result showed that optimum reaction conditons of esterification were as follows ： molar ration of SA/EG was 1 ： 1.8, cata- lyst was stannous octoate, amount of catalyst was 0. 3 %, the pre-esterification temperature was 180 ℃, the temper- ature of polycondensation under reduced pressure was 160 ℃, choosing the degree of vacuum was 1.99 kPa and the reaction time was 5 h. The esterification ratio of the product was 99%, the hydroxyl value was around 105 mgKOH/g and the acid value was 0. 91 mgKOH/e.

关 键 词：丁二酸 辛酸亚锡 丁二酸聚酯二醇 合成 

分 类 号：TQ225.241[化学工程—有机化工]