镁合金铸轧过程中表面点状偏析形成机制  

Formation of Surface Bleeding Segregations during Twin-Roll Casting of Magnesium Alloys

作　　者：翁文凭[1,2] 邓康[1] 任忠鸣[1] 迟之东[2] 陈琦[2] 

机构地区：[1]上海大学,上海200072 [2]苏州有色金属研究院有限公司,江苏苏州215026

出　　处：《稀有金属材料与工程》2013年第10期2093-2096,共4页Rare Metal Materials and Engineering

基　　金：江苏省自然科学基金面上项目(BK2010249);苏州市科技支撑计划(SG201227);中色科技股份公司科技发展基金项目(2008YK02)

摘　　要：采用金相检测与扫描电镜观察等方法,分析了镁合金铸轧板坯表面点状偏析的微观组织与微区成分,结果表明:表面点状偏析由富含Al、Zn溶质元素的金属间化合物组成,而Mn元素在偏析区域内含量与基体相同;偏析区域内组织主要为细小等轴晶粒。采用快速停车的方式获取镁合金铸轧板坯急停试样,分析镁合金铸轧板坯表面点状偏析的形成过程;在此基础上,分析了溶质Al、Zn和Mn元素在偏析区域内分布特征。Microstructure and micro-area chemical composition of surface bleeding segregations of magnesium alloy strips processed via twin-roll casting were investigated by OM,SEM and WDS.The results indicate that surface bleeds are composed of solute-rich intermetalics of A1.and Zn element,the percentage composition of Mn element in surface bleeds is similar to that of the matrix alloy.The structure of surface bleeds changes into equiaxed grain with fine grain size.Stop-samples were achieved by abruptly interrupting casting for analyzing the solidification and deformation characters in the set-back of magnesium alloys strips,and the formation mechanism of surface bleeds were discussed.Furthermore,the characteristics of solute elements distribution in surface bleedings including Al,Zn and Mn elements were discussed.

关 键 词：镁合金 双辊铸轧 表面点状偏析 形成机制 

分 类 号：TG292[金属学及工艺—铸造]