磁性壳聚糖微球的生物相容性  

Biocompatibility of magnetic chitosan microspheres

作　　者：王子妤[1] 董菊[1] 张东生[2] 

机构地区：[1]南京中医药大学基础医学院,江苏省南京市210023 [2]东南大学医学院,江苏省南京市210009

出　　处：《中国组织工程研究》2013年第42期7414-7419,共6页Chinese Journal of Tissue Engineering Research

基　　金：国家自然科学基金资助项目(81201187);南京中医药大学基础青年科技创新基金资助项目(10JCQN08)~~

摘　　要：背景:采用壳聚糖对磁性氧化铁纳米颗粒表面进行改性,一方面可改善磁性纳米氧化铁颗粒的团聚性,增加其稳定性,另一方面将来可用于肿瘤热疗及基因治疗。目的:制备将来可用于肿瘤热疗及基因治疗的磁性壳聚糖微球,评价其生物相容性。方法:采用改良的化学沉淀法制备磁性氧化铁纳米颗粒。采用超声乳化法将壳聚糖加入到磁性氧化铁纳米颗粒中制备磁性壳聚糖微球,进行以下实验:①MTT实验检测磁性壳聚糖微球浸提液的细胞毒性:分别以1640培养液、聚丙烯酰胺单体溶液、100%,75%,50%,25%的磁性壳聚糖微球浸提液培养L-929细胞。②溶血实验:在兔抗凝血中分别加入磁性壳聚糖微球浸提液、生理盐水及蒸馏水。③微核实验:在昆明小鼠腹腔分别注射含氧化铁磁流体5,3.75,2.5,1.25 g/kg的磁性壳聚糖微球混悬液、环磷酰胺及生理盐水。结果与结论:磁性壳聚糖微球粒径200-300 nm,分散效果有所提高。不同浓度的磁性壳聚糖微球浸提液对L-929细胞毒性为1级,属对细胞无毒性范畴。磁性壳聚糖微球浸提液的溶血率为0.69%,小于5%,符合医用材料的溶血实验要求。磁性壳聚糖微球混悬液未导致细胞DNA断裂和非整倍体化,未导致微核产生的遗传毒理作用,材料无致畸或致突变作用,因此磁性壳聚糖微球具有良好的生物相容性。BACKGROUND：Chitosan modification for magnetic iron oxide nanoparticles can improve the agglomeration and stability of magnetic iron oxide nanoparticles, and in addition, it can be used for tumor hyperthermia and gene therapy in the future. OBJECTIVE：To explore the biocompatibility of magnetic chitosan microspheres which have the potential application in tumor hyperthermia and gene therapy. METHODS：Magnetic iron oxide nanoparticles were prepared using the modified chemical precipitation. Phacoemulsification method was used to add chitosan into magnetic iron oxide nanoparticles in the preparation of magnetic chitosan microspheres. Then, the fol owing tests were performed. （1） Cytotoxicity test：L-929 cells were cultured in 1640 medium, polyacrylamide monomer solution, 100%, 75%, 50%, 25%of magnetic chitosan microsphere extracts. （2） Hemolysis test：Magnetic chitosan microspheres leaching solution, saline and distil ed water were added. （3） Micronucleus test：Kunming mice were intraperitoneal y injected with magnetic chitosan microspheres suspension containing 5, 3.75, 2.5, 1.25 g/kg iron oxide magnetic fluid, cyclophosphamide and saline, respectively. RESULTS AND CONCLUSION：Magnetic chitosan microspheres of 200-300 nm in diameter had an increased dispersion effect. The result of 3-（4,5-dimethylthiazol-2-yl）-2,5-diphenyltetrazolium bromide assay showed that the toxicity of the material on L-929 celllines belonged to no cytotoxicity. In the hemolysis test, the hemolysis rate of magnetic chitosan microspheres was 0.69%far less than 5%. In the micronucleus test, magnetic chitosan microspheres suspension did not cause DNA fragmentation and aneuploidy, and did not result in genetic toxicological effects produced by micronuclei. The magnetic chitosan microspheres did not appear with cacogenesis and mutagenesis. From the results, magnetic chitosan microspheres are a kind of high biocompatibility material.

关 键 词：微球体 壳聚糖 生物相容性材料 骨基质 

分 类 号：R318[医药卫生—生物医学工程]