Photoluminescent properties of tunable green-emitting oxynitride （Baa-xSrx）Si6012N2 ：Eu2＋ phosphor and its application in white LEDs  

出　　处：《Journal of Rare Earths》2013年第10期944-949,共6页稀土学报（英文版）

基　　金：Project supported by National High Technology Research and Development Program of China （2010AA03A404）, National Natural Science Foundation of China （51102021）, and Beijing Natural Science Foundation （2102022）

摘　　要：Green emitting Eu2＋-doped （Ba3_xSrx）Si6012N2 solid solutions were synthesized through solid state reaction at 1350 ℃ for 10 h under a N2/H2 atmosphere. The XRD patterns revealed that the solid solution series of （Ba3 x-ySrx）Si6Ol2N2：yEu2＋ with x value ranging from 0-0.6 were established. An efficient and intense tunable green light was observed by varying the cation Sr/Ba ratio. The emission spectra exhibited an entire shift towards long wavelength with increasing ofx value, which was caused by large crystal field splitting and Stokes shift. The x value dependence of emission intensity was discovered and explained by the enhanced probability of electron from excited 4f state to 5d ground state via nonradioactive transition. Highly thermal stability and feasible color coordinates were verified. White LEDs with excellent photochromic properties were fabricated by packing GaN based blue chips and （Ba Sr）3Si6012N2：Eu2＋ phosphors. All results indicated that the （Ba3_xSrx）SirO12N2：Eu2＋ phosphors were confirmed to be a promising candidate for pc-white LEDs in solid state lighting.Green emitting Eu2＋-doped （Ba3_xSrx）Si6012N2 solid solutions were synthesized through solid state reaction at 1350 ℃ for 10 h under a N2/H2 atmosphere. The XRD patterns revealed that the solid solution series of （Ba3 x-ySrx）Si6Ol2N2：yEu2＋ with x value ranging from 0-0.6 were established. An efficient and intense tunable green light was observed by varying the cation Sr/Ba ratio. The emission spectra exhibited an entire shift towards long wavelength with increasing ofx value, which was caused by large crystal field splitting and Stokes shift. The x value dependence of emission intensity was discovered and explained by the enhanced probability of electron from excited 4f state to 5d ground state via nonradioactive transition. Highly thermal stability and feasible color coordinates were verified. White LEDs with excellent photochromic properties were fabricated by packing GaN based blue chips and （Ba Sr）3Si6012N2：Eu2＋ phosphors. All results indicated that the （Ba3_xSrx）SirO12N2：Eu2＋ phosphors were confirmed to be a promising candidate for pc-white LEDs in solid state lighting.

关 键 词：OXYNITRIDE PHOSPHOR solid solution white LEDs rare earths 

分 类 号：TN312.8[电子电信—物理电子学] TN304.26