阴离子环境对铁基高温变换催化剂结构与性能的影响  

The Effect of Anions on Structure and Catalytic Properties of the Fe-based High Temperature Shift Catalyst

作　　者：姜浩强[1] 何润霞[1] 武芳[1] 智科端[1] 周晨亮[1] 张万华[1] 刘全生[1] 

机构地区：[1]内蒙古工业大学化工学院,内蒙古工业催化重点实验室,呼和浩特010051

出　　处：《内蒙古工业大学学报（自然科学版）》2013年第3期189-193,共5页Journal of Inner Mongolia University of Technology：Natural Science Edition

基　　金：国家自然科学基金(21066008);内蒙古自然科学基金(2009ZD01);内蒙古人才基金及内蒙古工业大学"煤化工特色学科"(2008NRC006)资助

摘　　要：采用湿法共沉淀工艺制备了不同阴离子环境下的铁基高温变换催化剂,利用XRD、BET、TG-DTA、TEM和活性测试等对催化剂样品的结构和性能进行比较研究。结果表明,阴离子环境对催化剂制备过程中所生成前驱体的结构影响较大,最终导致成品催化剂性能相差很大。SO2-4环境下制备的催化剂活性较好,500℃耐热180min后350℃的活性可达24.52%,而Cl-环境下制备的催化剂活性较差,500℃耐热后350℃的活性为6.94%。The Fe -based high temperature shift catalysts were prepared by the wet co -precipitation method, which were characterized by XRD , SBET and TG-DTA and tested for water-gas shift reaction.The results showed that anions types had significant effects on the structure and performance of precursor which generated during the process of preparation , finally caused product catalyst performance vary widely .The catalytic activity of sample in the SO 2-4 environment was better , which was 24 .52% at 350℃ after heat resistance（500℃,180min）;the catalytic activity of sample in the Cl -environment was lower, which was 6. 94%at 350℃after heating resistance（500℃,180min）.

关 键 词：高温水煤气变换 铁基催化剂 阴离子环境 活性 

分 类 号：TQ426.6[化学工程]