连续玻纤增强聚烯烃预浸带的力学性能  

Mechanical properties of continuous glass fiber reinforced polyolefin prepreg tapes

作　　者：刘雪静[1] 谭洪生[1] 李丽平[1] 谭哲兴[1] 

机构地区：[1]山东理工大学材料科学与工程学院,山东淄博255091

出　　处：《山东理工大学学报（自然科学版）》2013年第5期1-4,9,共5页Journal of Shandong University of Technology:Natural Science Edition

基　　金：山东省自然科学基金资助项目(ZR2011EMM012)

摘　　要：分别以五种聚烯烃树脂为基体，采用自行设计的浸渍模具制备了连续玻璃纤维增强聚烯烃预浸带，并采用热模压机将预浸带压制成相应的板材．研究了五种基体树脂、纤维含量、纤维分布对复合材料力学性能的影响．结果表明，加入玻纤后复合材料的拉伸强度、弯曲强度大幅度提高，纤维分布对材料的弯曲性能影响较大；纤维含量0～70％范围内，随纤维用量的增加，复合材料的力学性能提高；在709／6～759／6范围内，复合材料的力学性能随纤维含量的增加而降低．动态力学分析表明，加入纤维后明显提高了复合材料的抗形变能力．Five kinds of polyolefin resins were used as matrix, the continuous glass fiber rein- forced polyolefin prepreg tapes were prepared by a self-designed impregnation mold and the prepreg tapes were pressed into the corresponding plate using a hot stamping press. The influ- ences of five kinds of polyolefin, fiber content and fiber distribution on mechanical properties of composites were studied. The results show that the tensile and flexural strengths increase obvi- ously with the addition of the glass fibers, and the influence of fiber distribution on flexural prop- erty of the composites was more obviously than that of other property. In the range of 0~70~, the mechanical properties of the composites increased with the increase of the fiber content. In the range of 70-75%, the mechanical properties of the composites decreased with the increase of the fiber content. The result of dynamic mechanical behavior shows that the deformation re- sistance of the composites enhanced evidently with the increase of the glass fiber content.

关 键 词：连续纤维增强 玻璃纤维 浸渍带 力学性能 

分 类 号：TQ327.1[化学工程—合成树脂塑料工业]