侧链含分散红类染料基团的聚(氨酯-酰亚胺)的合成与表征  

Synthesis and Characterization of Poly(urethane-imide)s Containing a Disperse Red Type Chromophore in the Side chain

作　　者：朱娜[1] 隋郁[1] 印杰[1] 刘燕刚[1] 朱子康[1] 王宗光[1] 

机构地区：[1]上海交通大学化学化工学院,上海200240

出　　处：《高等学校化学学报》2000年第11期1771-1775,共5页Chemical Journal of Chinese Universities

基　　金：上海市科委新材料研究中心重点基金! (批准号 :97JC14 0 14 )资助

摘　　要：采用两步法合成了 4种侧链含偶氮染料发色团分散红 -1 9的新型聚 (氨酯 -酰亚胺 ) ( PUI) :先合成含染料发色团的二异氰酸酯 ,再进一步和二酐单体缩合生成 PUI.用红外光谱、紫外 -可见光谱、DSC和 TGA等手段对合成的 PUI进行表征 .所有 PUI在～ 4 90 nm处都有一强吸收峰 .PUI可溶于强极性非质子溶剂 ,如NMP,DMAc,DMF,DMSO和 1 ,4 -丁内酯 ,有些甚至在常用的低沸点溶剂如 THF中也可溶解 .PUI的特性粘数在 0 .1 6～ 0 .31 d L/ g范围内 .其玻璃化转变温度 ( Tg)在 1 71～ 2 1 1℃范围内 ,明显高于侧链型非线性光学聚氨酯 ( PU) .以刚性相对较大的六氟异丙叉基二 ( 3,4 -邻苯二甲酸酐 ) ( 6FDA)和甲苯 -2 ,4 -二异氰酸酯( TDI)为单体的 PUI具有比以二苯醚 -3,3′,4 ,4′-四甲酸二酐 ( OPDA)和 4 ,4′-二异氰酸酯二苯甲烷 ( MDI)为单体的 PUI更高的 Tg.PUI的 TGA曲线上有两个明显的失重台阶 ,起始热分解温度大约在 30 0℃左右 .Four novel poly(urethane imide)s(PUIs) containing a diazo nonlinear optical chromophore in the side chain were synthesized by a two step process, which includes preparation of diazo chromophore containing diisocyanates followed by the condensation reaction with dianhydrides. The PUIs obtained were characterized by FTIR spectroscopy, UV Vis spectroscopy, DSC and TGA. All PUIs exhibit a maximum UV Vis absorption of the diazo chromophore at the wavelength of about 490 nm. They are soluble in aprotic solvents such as NMP, DMAc, DMF, DMSO and 1,4 butyrolactone. Some are even soluble in common low boiling point solvents such as THF. The high organo solubility of PUIs results from the existence of the flexible urethane moiety in the backbone and a side chain chromophore, which leads to loose chain packing and enlarge free volume. The intrinsic viscosities of PUIs are 0.16~0.31 dL/g. The PUIs possess glass transition temperatures( T g) at 171~211 ℃, which are much higher than the corresponding side chain nonlinear optical(NLO) polyurethanes. PUIs based on 4,4′ (hexafluoroisopropylidene) diphthalic anhydride(6FDA) and tolulene 2,4 diisocyanate(TDI) possess higher T g than those based on 3,3′ , 4,4′ diphenylether tetracarboxylic acid dianhydride(OPDA) and methylenediphenylene diisocyanate(MDI). Two steps of weight loss are found in TGA curves of PUIs. The initial decomposition temperatures of PUIs are around 300 ℃, which is attributed to the thermal decomposition of the urethane moiety and the side chain chromophore.

关 键 词：聚(氨酯-酰亚胺) 二阶非线性光学 合成 表征 

分 类 号：O633.5[理学—高分子化学] O437[理学—化学]