陶瓷/不锈钢层状复合材料研究  

The Research on Ceramic/Stainless Steel Layer Complex Material

作　　者：温建平[1] 曾辉[1] 毛宇晖[1] 张海宁[1] 黄福传 

机构地区：[1]嘉应学院,梅州514015 [2]富大陶瓷有限公司,梅州514200

出　　处：《佛山陶瓷》2013年第11期16-19,共4页Foshan Ceramics

基　　金：广东省教育部产学研结合项目资金资助;项目编号:2011B

摘　　要：对1.0 mm的不锈钢钢板进行抛砂粗化处理,用本地瓷土制备2.0 mm厚度的陶瓷片,用环氧树脂粘接剂将陶瓷片和不锈钢薄板多层粘接固化,制备了陶瓷/不锈钢层状复合材料。对制备的复合材料进行了性能测试,断裂韧性达到9.6 MPa·m1/2。用层状复合材料进行冲击磨损试验,耐磨性高出高锰钢160%,将高锰钢镶嵌层状复合材料后,使零件的使用寿命提高了2倍。The ceramic/stainless steel layer complex material was prepared by adhesiving ceramic sheet prepared throngh clay with the thickness of 2.0 mm,and stainless steel which had been roughened with thickness of 1.0 mm.The performance of prepared complex material had been tested.The fracture toughness of material is over 9.6MPa ·min. hnpact wear experiments were conducted, the test indicated that wear-resistance of layered complex material were up to 1.6 times larger than high manganese steel. Within inlaying complex material,the service life of high manganese steel hammer is 2 times longer than before.

关 键 词：不锈钢 陶瓷 复合材料 

分 类 号：TB333[一般工业技术—材料科学与工程]