电磁连铸半连续铸造和轧制AZ41M镁合金的组织与性能  

Microstructure and properties of magnesium alloy AZ41M made by semi continuous casting asisted by electromagnetic continuous casting and rolling

作　　者：易更[1] 洪利国 成建国[1] 贺勇[1] 李胜杰[1] 朱宇瑾[1] 

机构地区：[1]中国兵器科学研究院宁波分院,浙江宁波315103 [2]宁波市江北洪塘金属压延厂,浙江宁波315033

出　　处：《兵器材料科学与工程》2013年第6期61-64,共4页Ordnance Material Science and Engineering

摘　　要：采用电磁连铸半连续铸造和轧制工艺方法，利用X线荧光光谱仪、金相显微镜对AZ41M镁合金化学成分、铸态微观组织及板材轧制态、退火态微观组织进行分析以调整工艺参数。结果表明：基本工艺制度为浇注温度700~710℃、磁场频率2.5 kHz、磁场功率0-10 kW、冷却水量1.2 T/h、均匀化退火处理400℃×16 h，空冷、换向轧制；每道次后均改变轧向，每道次压下量为5%。In order to optimize the process parameters of electromagnetic continuous casting of semi-continuous casting and rolling process,X ray fluorescence spectrometer and metallurgical microscope were used to analyze chemical composition,the microstructures of as-cast,as-rolled and as-annealed magnesium alloy AZ41M. The results show that the basic process parameters are as follows：pouring temperature 700 to 710℃,magnetic field frequency 2.5 kHz,magnetic power 0 to 10 kW, cooling water 1.2 T/h,homogenizing annealing treatment 400℃for 16 h,air-cooling. The rolling direction should be changed after per pass,of which the rolling reduction rate is 5%.

关 键 词：AZ41M镁合金 半连续铸造 轧制 板材 退火 

分 类 号：TG146.22[一般工业技术—材料科学与工程]