pH值对电流化学镀复合结构丝的性能影响研究  

Influence of pH value on the properties of the composite wires by chemical deposition

作　　者：栾红艳[1] 李欣[1] 王蕊丽[1,2] 潘海林[1] 陈德禄[1] 赵振杰[1] 

机构地区：[1]华东师范大学物理系纳光电集成与先进装备教育部工程研究中心,上海200062 [2]上海海洋大学物理实验室,上海201306

出　　处：《华东师范大学学报（自然科学版）》2013年第6期127-132,共6页Journal of East China Normal University(Natural Science)

基　　金：上海汽车工业科技发展基金会(SAISTDF/12-06);华东师范大学科研创新基金(78210142;78210183)

摘　　要：采用电流化学镀工艺,在直径为100μm的铜丝上通以150 mA的直流电流,制备了NiCoP/CuBe复合结构丝,研究了镀液pH值对复合结构丝镀层的形貌、镀速、成分、磁性能和GMI效应的影响.研究发现,镀液pH值的改变会引起致密性、镀速、镀层成分和磁性能的变化,结果影响到材料的磁阻抗比和特征频率.pH值为8.4时,得到最大阻抗比为868%.Composite wires of 100 μm diameter CuBe coated with a layer of NiCoP were prepared by chemical plating,and dc current of 150 mA got through CuBe wires during the process.The influence of pH value on the composite wires was studied in terms of morphology,deposition speed,composition,magnetic property and the GMI effect.The results showed that the pH value influenced GMI effect and critical frequency by changing the roughness of materials,deposition speed,the coating composition and magnetic structure.The maximum GMI effect of 868% is obtained at the pH value of 8.4. ：

关 键 词：PH值 复合结构丝 化学镀 GMI效应 