胶原纤维对Cr^(3+)的吸附性能  被引量:4

Adsorption Performance of Collagen Fiber Toward Cr^(3+)

在线阅读下载全文

作  者:王学川[1] 步巧巧[1] 强涛涛[1] 

机构地区:[1]陕西科技大学教育部轻化工助剂化学与技术重点实验室,陕西西安710021

出  处:《精细化工》2013年第12期1408-1412,1422,共6页Fine Chemicals

基  金:国家自然科学基金项目(21276151);陕西省教育厅项目(12JK0594);博士后基金项目(2012M521733);陕西省科研创新团队项目(2013KCT-08);陕西科技大学研究生创新基金项目~~

摘  要:以铬粉溶液为处理对象,研究了胶原纤维对Cr3+的吸附性能;通过单因素实验,考察了pH、温度、时间、铬液初始质量浓度、吸附剂用量以及盐离子浓度(Na+、Ca2+)对吸附过程的影响,结果表明,胶原纤维对Cr3+具有较强的吸附能力,吸附的最佳pH=4.5,最适温度40℃,在最佳吸附条件下,胶原纤维对Cr3+的吸附容量高达90mg/g,对于一定量的铬粉溶液,吸附容量随着Cr3+初始质量浓度的增大而增加,随着吸附剂用量的增加而减小,随着时间的延长先增加后趋于平缓。溶液中Na+、Ca2+离子的存在会抑制吸附过程的进行,并且随着离子浓度的增加,抑制作用增强;对Cr3+在胶原纤维上的吸附热力学和吸附动力学进行了研究,结果表明,Freundlich等温方程和二级速率方程能够更好地描述Cr3+在胶原纤维上的吸附行为。The characteristics of adsorption of Cr3+ on the collagen fiber (CF) were studied with chromium solution as processing target. The effects of temperature, time, pH, adsorbent dosage, initial mass concentration and salt ion concentration (Na + , Ca2+ ) on the adsorption process were respectively studied through the single factor experiments. The results indicate that the collagen fibers have strong adsorption ability to Cr3+ and the adsorption capacity can be up to 90 mg/g, and the optimal pH and temperature of adsorption were 4.5 and 40 ℃ , respectively. For a certain amount of chromium solution, the adsorption capacity was increased with the increase of initial concentration of Cr3+ , but decreased along with the increase of adsorbent dosage. With the extension of time, the adsorption capacity increased gradually and finally reached adsorption equilibrium. The salt ions in the solution had inhibitory effect on the adsorption process, and the inhibition was enhanced with the increase of ion concentration. The adsorption thermodynamics and adsorption dynamics were studied by comparison, and it was found that the Freundlich equation and Pseudosecond-order kinetic model can better describe the adsorption behavior of Cr3+ on the collagen fiber.

关 键 词:胶原纤维 CR^3+ 吸附性能 水处理技术与环境保护 

分 类 号:TQ424.3[化学工程]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象