敏化处理304不锈钢局部腐蚀行为的扫描微电极法研究  

Localized Corrosion Behavior of Sensitized 304 Stainless Steel by Scanning Reference Electrode Technique

作　　者：叶陈清[1,2] 胡融刚[1,3] 侯瑞青[1] 王小平[1] 杜荣归[1] 林昌健[1] 

机构地区：[1]厦门大学固体表面物理化学国家重点实验室,化学化工学院化学系,福建厦门361005 [2]宁德师范学院化学与环境科学系,福建宁德352100 [3]贵阳学院化学与材料工程学院,贵州贵阳550005

出　　处：《电化学》2013年第6期507-511,共5页Journal of Electrochemistry

基　　金：国家自然科学基金项目(No.21021002)资助

摘　　要：通过扫描微电极法研究敏化处理奥氏体不锈钢(304ss)的局部腐蚀行为,并结合传统电化学方法及光学显微镜进行测试观察.结果表明,在10%FeCl3溶液未敏化处理(304ss-NS)或550oC轻度敏化处理(304ss-S1)的不锈钢倾向于发生点腐蚀,而650oC(304ss-S2)或750oC(304ss-S3)深度敏化处理不锈钢则倾向于发生晶间腐蚀.Based on a home-built setup of scanning reference electrode technique, and combined with conventional electrochemical measurements, the localized corrosion behavior of sensitized 304 stainless steel（304ss） had been investigated in this work. The results showed that the non-sensitized 304ss or 304ss sensitized at 550℃ was susceptible to pitting; while 304ss sensitized at 650℃ or 750℃ suffered severe intergranular corrosion in 10% FeCl3 solution.

关 键 词：304不锈钢 敏化处理 扫描微电极技术 局部腐蚀 晶间腐蚀 

分 类 号：TG174.3[金属学及工艺—金属表面处理] TG142.71[金属学及工艺—金属学]