(Bi_(3.15)Nd_(0.85))(Ti_2Fe_(0.5)Co_(0.5))O_(11.5)陶瓷的制备及多铁性能表征  

Preparation and multiferroic properties of (Bi_(3.15)Nd_(0.85))(Ti_2Fe_(0.5)Co_(0.5))O_(11.5) ceramics

作　　者：肖君[1] 魏聪[1] 孔祥鹏[1] 苏鹏[1] 杨辅军[1] 陈晓琴[1] 

机构地区：[1]湖北大学物理学与电子技术学院,湖北武汉430062

出　　处：《湖北大学学报（自然科学版）》2014年第1期64-67,共4页Journal of Hubei University：Natural Science

基　　金：国家自然科学基金(51002047;11274101)资助

摘　　要：采用改进的固相反应法制备（ Bi3.15 Nd0.85 ） （ Ti2 Fe0.5 Co0.5 ） O11. 5 陶瓷．多铁性能测试结果表明，陶瓷样品具有室温多铁性．样品的剩余磁化为～77memu／g，剩余极化为～1．7μC／cm2，且磁场对介电频谱的影响证实该陶瓷样品的室温磁电耦合效应．The layer-structured （ Bi3.15 Nd0.85 ） （ Ti2 Fe0.5 Co0.5 ） O11. 5 ceramic was synthesized by using the improved solid-state reaction method. The multiferroic properties of the sample at room- temperature by ferroelectric and magnetic measurements was proved. The sample presented large magnetic response with 2Mr≈77 memu/g and a weak ferroelectric （FE） with 2Pr≈1. 7μC/cm2. The e{fect of magnetic field on relative dielectric constant clearly indicated the magnetoelectric effects （ME） of the sample.

关 键 词：多铁性 铁电性 铁磁性 磁电耦合效应 

分 类 号：TB34[一般工业技术—材料科学与工程]