钽、铌、钛的表面特性与生物相容性  

Surface characteristics and biocompatibility of Ta, Nb and Ti

作　　者：吴锋[1] 董兵辉[2] ALAJMI Zafer 付涛[2] 

机构地区：[1]西安交通大学医学院,西安710061 [2]西安交通大学生命科学与技术学院,西安710061

出　　处：《中国口腔种植学杂志》2013年第4期169-171,共3页Chinese Journal of Oral Implantology

基　　金：陕西省科技计划(2007K06-08);中央高校基本科研业务费专项资金(xjj2011096)资助项目

摘　　要：目的:筛选心血管支架材料。方法:考察Ta、Nb、Ti的表面特性、血液相容性和内皮化能力。结果:Ta表面平整,Nb、Ti表面较为粗糙;三者均表现出弱的疏水性和良好的耐蚀性。三种试样的溶血率均低于5%,Ta表面粘附的血小板较少。内皮细胞培养3天时,Ta表面的细胞增殖活性较好,而Nb表面的细胞生长较差。结论:Ta是一种良好的心血管支架材料。To select cardiovascular stent materials. Methods： Investigating surface characteristics, hemocompatibility and endothelium of Ta, Nb, Ti. Results： Ta has smooth surface, but Nb and Ti have rougher ones. They all have weak hydrophobicity and good corrosion resistance. Their hemolysis rates are all below 5%, and Ta has less adhered platelets at the surface. When cultured for 3 days, endothe- lial cells have higher proliferative activity at Ta surface, but grow worse at Nb surface. Conclusion： Ta is a good material for cardiovascular stents.

关 键 词：钽 铌 钛 腐蚀 血液相容性 内皮化 

分 类 号：R318.08[医药卫生—生物医学工程]