固相合成Cr掺杂LiFePO_4/C及其电化学性能  

Electrochemical Properties of Cr Doped LiFePO_4 /C Prepared by Solid-State Synthesis

作　　者：刘红飞[1] 杨海霞[2] 

机构地区：[1]宁夏大学物理电气信息学院,宁夏银川750021 [2]中国矿业大学银川学院土木工程系,宁夏银川750021

出　　处：《广州化工》2013年第24期59-60,104,共3页GuangZhou Chemical Industry

摘　　要：采用固相合成法制备了Li1-x Cr x FePO4/C(x=0,0.01,0.02,0.03,0.04),实验结果表明:采用固相合成法制备的Cr掺杂LiFePO4/C具有完善的LiFePO4橄榄石型晶体结构。发现在Cr的掺入量为0.02摩尔分数时,表现出较好的循环性能和充放电性能,在0.1 C倍率充放电时,放电比容量为159.8 mAh/g。Li1-xCrxFePO4/C was synthesized by the solid state reaction. The results showed that the products were well crystallized. The optimum dosage of Cr was 0.02 with better rate performances and cycling stability. Electrochemical tests showed that the capacities reach 159. 8 mAh/g, when the charge discharge was 0. 1.

关 键 词：锂离子电池 正极材料 X射线衍射分析 铬掺杂 

分 类 号：TQ912.9[化学工程]