曲轴用非调质钢C38N2奥氏体长大行为及热塑性研究  

Austenite grain growth behavior and hot ductility of non-quenched and tempered steel C38N2 for crankshaft

作　　者：杨忠[1,2] 寇玉山 王海龙 郭俊国[1] 张燕东 刘雅政[1] 

机构地区：[1]北京科技大学材料科学与工程学院,北京100083 [2]西宁特殊钢集团有限责任公司,青海西宁810005

出　　处：《金属热处理》2014年第2期30-33,共4页Heat Treatment of Metals

摘　　要：研究了曲轴用非调质钢C38N2在不同加热温度和加热时间下的奥氏体晶粒长大行为及高温下的热塑性，并建立了奥氏体晶粒长大的数学模型。结果表明，加热时间30min时，奥氏体晶粒粗化温度和铌迅速大量固溶的开始温度为1050℃；在900～1050℃和1050～1250℃两个温度区间内，奥氏体晶粒长大方程分别为D=1．01×10^3·t^0.21·exp（-5．33×10^4／（RT））和D=8．77×10^6·t^0.21·exp（-1．59×10^5／（RT））；高热塑性温度范围为800～1200℃，1100℃时热塑性最好。The austenite grain growth behavior under different heating temperatures and holding time and the hot ductility of non-quenched and tempered steel C38N2 for crankshaft were investigated. The results show that the austenite grain coarsening temperature and the start temperature when niobium heavy and rapidly solution is 1050 ℃. Growth models of austenite grain in the temperature ranges of 900-1050 ℃ and 1050-1250℃ are described as D = 1.01 ×10^3 · t^0.21 · exp （ - 5.33 ×10^4/（RT） ） and D = 8.77 × 10^6 · t^0.21 · exp （ - 1.59 × 10^5/ （RT） ） , respectively. The steel has good hot ductility in the temperature range 800-1200 ℃ , and has the best hot ductility when the heating temperature is 1100 ℃.

关 键 词：非调质钢 奥氏体 晶粒长大 热塑性 

分 类 号：TG142.1[一般工业技术—材料科学与工程]