Synthesis and Characterization of Biodegradable Alternating Polyesteramides from Mixed Diamidediols and Sebacic Acid  

作　　者：SUN Huiyun YIN Tiao LI Yue ZHAO Jingbo ZHANG Zhiyuan ZHANG Junying 

机构地区：[1]Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education,College of Materials Science and Engineering, Beo'ing University of Chemical Technology, Beijing 100029, P R. China

出　　处：《Chemical Research in Chinese Universities》2014年第1期168-175,共8页高等学校化学研究（英文版）

基　　金：Supported by the National Natural Science Foundation of China（Nos.50873013, 21244006）.

摘　　要：A series of polyesteramide prepolymers[PrePEA（0/4,8）s] having mixed alternating bisesterdiamide units was synthesized via melt polycondensation from N,N＇-bis（2-hydroxyethyl）oxamide（0） and N,N＇-bis（2-hydroxyethyl）-adipamide（4） with sebacic acid（8） at different molar ratios.Chain extension of them was conducted with 2,2＇-（1,4-phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders.The chain extended polyesteramides[ExtPEA（0/4,8）s] were characterized by proton nuclear magnetic resonance（1H NMR）,gel permeation chromatography（GPC）,differential scanning calorimetry（DSC）,thermogravimetry analysis（TGA）,wide angle X-ray scattering,tensile test and enzymatic degradation.The results show that ExtPEA（0/4,8）s were crystalline polyesteramides.They had Tm up to 136.5 ℃ and initial decomposition temperature above 297.5 ℃.They crystallized in similar crystallites into Nylon-66 and degraded under the catalysis of protease or lipase.They are thermoplastic materials with tensile strength up to 21.5 MPa and elongation at break above 64.0％.A series of polyesteramide prepolymers[PrePEA（0/4,8）s] having mixed alternating bisesterdiamide units was synthesized via melt polycondensation from N,N＇-bis（2-hydroxyethyl）oxamide（0） and N,N＇-bis（2-hydroxyethyl）-adipamide（4） with sebacic acid（8） at different molar ratios.Chain extension of them was conducted with 2,2＇-（1,4-phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders.The chain extended polyesteramides[ExtPEA（0/4,8）s] were characterized by proton nuclear magnetic resonance（1H NMR）,gel permeation chromatography（GPC）,differential scanning calorimetry（DSC）,thermogravimetry analysis（TGA）,wide angle X-ray scattering,tensile test and enzymatic degradation.The results show that ExtPEA（0/4,8）s were crystalline polyesteramides.They had Tm up to 136.5 ℃ and initial decomposition temperature above 297.5 ℃.They crystallized in similar crystallites into Nylon-66 and degraded under the catalysis of protease or lipase.They are thermoplastic materials with tensile strength up to 21.5 MPa and elongation at break above 64.0％.

关 键 词：Alternating polyesteramide POLYCONDENSATION Chain extension Diamidediol 