应用于NFC的低温烧结NiCuZn材料研究  

Study on Low Temperature Sintering NiCuZn Material Applied to NFC

作　　者：刘卫沪[1] 颜铄清[1] 李启凡[1] 陈中艳[1] 董丽[1] 冯则坤[1] 

机构地区：[1]华中科技大学光学与电子信息学院,湖北武汉430074

出　　处：《压电与声光》2014年第1期89-92,共4页Piezoelectrics & Acoustooptics

基　　金：广东省江门市2013重大科技专项基金资助项目

摘　　要：采用流延法制备了长×宽为125mm×125mm,厚最薄为50μm的铁氧体电磁屏蔽片。研究了电磁屏蔽片屏蔽近场噪声源能力与材料磁谱间的关系,同时研究了材料中的CuO含量及助烧剂Bi2O3的添加量对材料磁谱的影响。结果表明,电磁屏蔽片屏蔽近场噪声源的能力与材料在13.56MHz下的磁导率μ′及品质因数(Q)相关。CuO含量过大,材料的磁谱特性会变差;Bi2O3的添加量对材料的高频段磁谱性能影响不大。The ferrite electromagnetic shielding sheet with the size of 125 mm× 125 mm and the least thickness of 50μm were prepared by tape casting process.The magnetic spectrum of the ferrite and the performance of the electromagnetic shielding sheet under the condition of application have been studied.The effects of content of CuO and sintering-aid Bi2 O3 in the prescription of the material on the magnetic spectrum were also analyzed.The results indicated that the performance of the electromagnetic shielding sheet under the condition of application was related with the magnetic conductivityμand the value of Q of the material at 13.56 MHz.The magnetic spectrum would degrade when the content of CuO was too large.The magnetic properties of material at high frequency have little dependence with the additive amount of Bi2O3 in the prescription.

关 键 词：低温烧结铁氧体 近场通信(NFC) 电磁屏蔽片 

分 类 号：TM282[一般工业技术—材料科学与工程] TN384[电气工程—电工理论与新技术]