轧机轧制宽幅铝箔的工艺研究  

Study on Process of Rolling Wide Aluminum Foil on Mill

作　　者：张红香[1] 胡世军[1] 张代录[1] 

机构地区：[1]兰州理工大学数字制造技术与应用省部共建教育部重点实验室机电工程学院,甘肃兰州730050

出　　处：《热加工工艺》2014年第3期135-136,140,共3页Hot Working Technology

摘　　要：为了提高宽幅双零铝箔材的表面质量,制定了合理的试验方案和轧制工艺参数。反复进行现场对比试验,分析了试验结果,确定了轧制宽幅双零铝箔的最佳生产工艺参数。实践证明,所制定的生产工艺合理可用,而且轧制的宽幅双零铝箔材表面质量明显提高,满足了用户要求。In order to improve the surface quality of wide double zero aluminum foil, the reasonable testing scheme and process parameters of the rolling were constituted. The contrast tests on scene were carried out repeatedly. The test results were analyzed. The best production process parameters of rolling wide double zero aluminum foil were determined. Practice proves that the constituted production process is reasonably and usable, and the surface quality of rolled wide double zero aluminum foil is improved obviously, which meets the requirement of customers.

关 键 词：宽幅 铝箔 轧制 试验 