Effects of rare earth elements on sulphur and phosphorus impurities in deposited metal  

作　　者：范希营 郭永环 张亮 范晖 杨莉 

机构地区：[1]College of Mechanical and Electrical Engineering, Jiangsu NormalUniversity, Xuzhou, 221116

出　　处：《China Welding》2013年第4期63-67,共5页中国焊接（英文版）

基　　金：This project is supported by National Natural Science Foundation of China （ Grant No. 51305178） ; Xuzhou City Science and Technology Plan Projects （Grant No. XC12A013）.

摘　　要：In order to reduce sulphur （ S ） and phosphorus （ P ） impurities in deposited metal, a small amount of rare earth （RE） lanthanum （ La） and yttrium （Y） were added into the coating ofE4303 electrode, a low carbon steel electrode. The microstructures of deposited metal were analyzed with metalloscope, and then the content of S and P was examined by energy dispenive X-ray spectrometer （ EDXS ）, and by wavelength dispersive X-ray fluorescence （XRF） spectrometer for further examination. The results show that the proper addition of La and Y can be beneficial to the desulfurization and dephosphorization of the deposited metal. Certainly, difference in the addition amount of La and Y could lead to various desulfurization and dephosphorization efficiency, in which the former is more obvious than the latter. With the proper amount of La attd Y, there is finer microstructure in deposited metal, and mechanical properties are improved as well. The S content in deposited metal with added La and Y decreases by 44. 44 wt. % , while the P content 6. 67 wt. %, compared with that in deposited metal without La and II.In order to reduce sulphur （ S ） and phosphorus （ P ） impurities in deposited metal, a small amount of rare earth （RE） lanthanum （ La） and yttrium （Y） were added into the coating ofE4303 electrode, a low carbon steel electrode. The microstructures of deposited metal were analyzed with metalloscope, and then the content of S and P was examined by energy dispenive X-ray spectrometer （ EDXS ）, and by wavelength dispersive X-ray fluorescence （XRF） spectrometer for further examination. The results show that the proper addition of La and Y can be beneficial to the desulfurization and dephosphorization of the deposited metal. Certainly, difference in the addition amount of La and Y could lead to various desulfurization and dephosphorization efficiency, in which the former is more obvious than the latter. With the proper amount of La attd Y, there is finer microstructure in deposited metal, and mechanical properties are improved as well. The S content in deposited metal with added La and Y decreases by 44. 44 wt. % , while the P content 6. 67 wt. %, compared with that in deposited metal without La and II.

关 键 词：LANTHANUM YTTRIUM low carbon steel electrode deposited metal SULPHUR PHOSPHORUS 

分 类 号：O614.33[理学—无机化学] TG422.1[理学—化学]