高碳珠光体钢形变后的微观组织及力学性能研究  被引量:6

Microstructures and Mechanical Properties of High-carbon Pearlitic Steel After Deformation

在线阅读下载全文

作  者:樊雄[1,2] 

机构地区:[1]广西大学,广西南宁530001 [2]广西工业职业技术学院,广西南宁530001

出  处:《铸造技术》2014年第2期247-249,共3页Foundry Technology

基  金:广西省教育厅科研基金资助项目(桂教高教[2011]24号);广西工业职业技术学院科研基金资助项目(2011024JX005)

摘  要:研究了高碳珠光体T8钢在ECAP处理后的显微组织和力学性能。结果表明,利用多道次ECAP温变形能够使高碳珠光体钢组织呈现超微细化效果。复相组织中亚纳米级铁素体相纳米压痕杨氏模量和硬度分别为203 GPa和4.4 GPa。当纳米压痕深度超过100 nm后,杨氏模量对基底效应敏感度较低,而纳米压痕硬度出现较为明显的基底效应。The microstructures and mechanical properties of the high-carbon pearlitic steel T8 after ECAP deformation were investigated. The results show that the microstructures of the steel are ultrafine by multi-pass ECAP warm deformation. The nanoindentation Young’ modulus and hardness of subnano-sized ferrite in duplex microstructure are 203 GPa and 4.4 GPa, respectively. And when the distance from surface is above 100 nm, the sensibility of Young’ modulus to the matrix decreases, but the matrix effect is obvious for nanoindentation hardness.

关 键 词:高碳珠光体钢 纳米压痕 多道次ECAP 

分 类 号:TG142.21[一般工业技术—材料科学与工程]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象