Research on Directional Solidification Microstructure of CMSX-6 Superalloy

作　　者：徐基晨 马德新[1] 贾志宏[1] 赵玉涛[1] 朱翔[1] 张岩[1] 张若寰 

机构地区：[1]江苏大学材料科学与工程学院,江苏镇江212013

出　　处：《铸造技术》2014年第2期321-324,共4页Foundry Technology

基　　金：江苏省(工业)科技支撑计划项目资助(BE2011142);江苏省高校优秀科技创新团队计划项目资助(苏教科[2011]11号)

摘　　要：采用高速凝固法,在VDF-10定向凝固炉上,制备了CMSX-6镍基高温合金定向凝固试样。研究了距水冷铜板不同高度的凝固组织。结果表明,随着距水冷铜板高度的不断增加,CMSX-6合金的一次枝晶距也不断增大,其铸态组织由细枝状向粗枝状晶演变。同时距水冷铜板高度越低,枝晶干与枝晶间γ'相的尺寸越小,且枝晶间γ'相的形状趋向于规则的立方体形状。同时研究了枝晶间共晶组织的形貌特征,随着距水冷铜板高度增加,共晶尺寸不断地增大。The directional solidified nickel-base superalloy specimens were prepared by the method of high rate solidification in the VDF-10 directional solidification furnace. The solidification microstructures of different heights from the water-cooled copper disc were studied. The results show that, with the increase of the height, the primary dendrite arm spacing of CMSX-6 alloy increases obviously, the morphology transforms from coarse dendrite to fine dendrite. While with the decrease of the height, the shape of the γ’ precipitates decreases both in the dendrite arm and interdendritic, and the shape of γ’ precipitates in the indendrite tends to regular. At the last of the solidification process, the eutectic structure occurs, with the increase of the height, the shape of the eutectic increases.

关 键 词：镍基高温合金 凝固组织 一次枝晶间距 共晶组织 

分 类 号：TG27[金属学及工艺—铸造]