温镦挤模具磨损失效分析  

Failure Analysis on Wear of Warm Upset-Extrusion Die

作　　者：张亚龙[1] 徐新成[1] 栾怀超[1] 赵中华[1] 

机构地区：[1]上海工程技术大学工程实训中心,上海201620

出　　处：《热加工工艺》2014年第5期225-227,230,共4页Hot Working Technology

基　　金：上海市宝山区科学技术委员会产学研合作项目(CXY-2012-19)

摘　　要：对失效的H13温锻模具钢进行了分析,发现模具钢硬度、晶粒大小、合金元素含量基本符合标准。高温摩擦磨损实验及磨损形貌观测表明,模具磨损的主要形式为黏着磨损,氧化磨损和磨粒磨损。运用DEFORM-3D软件模拟分析了模具硬度和毛坯温度等工艺参数对模具磨损的影响,结果与实际磨损状况基本吻合。这可为延长模具寿命提供帮助。The failure of H13 steel warm forging die was analyzed. It is found that the hardness, crystal size and alloy elements content of the die are basically consistent with the standard. The high temperature friction and wear experiments and the observation of the wear morphology indicate that the main forms of die wear are oxidation wear, adhesive wear and abrasive wear. The impact of process parameters such as die hardness and blank temperature on the die wear was analyzed by using DEFORM-3D software. The results of the simulations are similar to the actual wear results. It can provide help for extending the service life of the die.

关 键 词：温镦挤 H13模具钢 磨损 失效分析 

分 类 号：TG375.4[金属学及工艺—金属压力加工]