有机硅改性丙烯酸脂在涤粘混纺织物抗起毛起球整理中的应用  

Application of Silicone-modified Acrylic Resin in Anti-pilling Finish oPolyester/Viscose Blended Fabric

作　　者：王晶晶[1] 

机构地区：[1]陕西工业职业技术学院化工与纺织学院

出　　处：《纺织导报》2014年第3期68-69,共2页China Textile Leader

摘　　要：将八甲基环四硅氧烷预乳化后与多组分丙烯酸酯共聚，采用种子乳液聚合法，合成有机硅改性丙烯酸树脂，并将其用于涤棉织物的抗起毛起球整理。本文主要探讨了乳液粒径大小、整理液浓度、焙烘温度和焙烘时间因素对整理效果的影响，确定优化工艺条件为乳液粒径75 nm，整理剂浓度5 g/L，焙烘温度160℃，时间1.5 min。在优化条件下，织物的抗起毛起球性能可达到4～5级，且织物的手感柔软。In order to improve anti-pilling tendency of polyester/viscose blended fabric, a kind of acrylic resin modified by silicone was synthesized through emulsion polymerization method. Then the emulsion was used in anti-pilling finish. Influences of diameter of emulsion particle, concentration of emulsion, baking temperature and time on finishing were researched. The optimum process conditions were as follows：diameter of emulsion particle 100 nm, emulsion concentration 5 g/L, baking at 160℃for 1.5 min.

关 键 词：有机硅改性丙烯酸酯 抗起毛起球 后整理 涤粘混纺织物 