温度对AZ80镁合金高温拉伸变形行为的影响  

Effect of temperature on high temperature tensile deformation behavior of AZ80 magnesium alloy

作　　者：刘运腾[1,2] 詹成伟[1] 周吉学[1] 唐守秋[1] 姜利坤[1] 

机构地区：[1]山东省科学院新材料研究所,山东济南250014 [2]山东省粘结材料重点实验室,山东济南250014

出　　处：《金属热处理》2014年第3期57-60,共4页Heat Treatment of Metals

基　　金：山东省自然科学基金(ZR2012EEL02)

摘　　要：通过高温拉伸试验，研究了AZ80镁合金在300～450℃、变形速率1mm／min条件下的高温变形行为。结果表明，在不同温度下，AZ80镁合金的高温拉伸应力-应变曲线均出现峰值，峰值应力随变形温度的升高而减小，而塑性随着变形温度的升高，先升高后降低。结合微观组织和断口形貌可以得出，AZ80镁合金在425℃下具有最好的变形能力。High temperature tensile deformation behavior of AZ80 magnesium alloy was studied at 300-450℃ and 1 mm/min deformation rate by high temperature tensile test. The resuhs show that under different temperature, there is a peak in the high temperature tensile stress- strain curves of the alloy. With the increase of deformation temperature, peak stress decreases and plasticity increases firstly and then decreases. Combined with the microstructure and fracture morphology it can be obtained that AZ80 magnesium alloy has the best deformability at 425℃.

关 键 词：AZ80镁合金 高温拉伸 温度 变形 

分 类 号：TG146.2[一般工业技术—材料科学与工程]