碳纳米管上沉积铂工艺的研究  被引量:10

Optimization of the technique for depositing platinum on carbon nanotubes

在线阅读下载全文

作  者:陈贵如[1] 徐才录[1] 毛宗强[2] 胡长建 魏秉庆[1] 梁吉[1] 吴德海[1] 徐景明[2] 

机构地区:[1]清华大学机械工程系 [2]清华大学核能技术研究院,北京100084

出  处:《清华大学学报(自然科学版)》2001年第2期5-7,共3页Journal of Tsinghua University(Science and Technology)

基  金:留学人员博士后基金资助项目

摘  要:对碳纳米管上沉积纳米级金属铂颗粒的工艺进行了探索性的研究。经处理后的碳纳米管与氯铂酸乙醇溶液 ,在一定温度时缓慢加入 H2 O2 ,Na2 S2 O4溶剂 ,然后在室温下电磁搅拌 ,清洗、过滤 ,烘干后的黑色粉末放置管式炉中在氮气气氛下保温。经 X射线衍射 (XRD)、扫描电子显微镜(SEM)、透射电子显微镜 (TEM)的检测结果表明 ,沉积在碳纳米管上的铂颗粒尺寸细小 ,分布均匀 ,无铂颗粒大块聚集。The technique for depositing Pt nanoparticles on carbon nanotubes was investigated and optimized. In the experiment hexachloroplatinic acid was mixed with alcohol and the treated carbon nanotubes, then fixed amounts of fresh H 2O 2 (30%) and Na 2S 2O 4 were slowly added into the mixture at 373K by stirring. After stirring for 24h the solution was washed by distilled water, filtered and dried. The mixture was then activated in an tube furnace with flowing N 2 at 973K for 1h. XRD, SEM, and TEM measurements showed small (~2nm in size), homogeneously distributed Pt particles on the carbon nanotubes. This result indicates that carbon nanotubes may be a strong candidate for Pt catalyst carrier materials.

关 键 词:碳纳米管 X射线衍射 扫描电子 显微镜 透射电子显微镜  沉积 工艺条件 

分 类 号:TB383[一般工业技术—材料科学与工程] TG146.33[金属学及工艺—金属材料]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象