ATRP-Template Dispersion Polymerization of Methacrylic Acid/PVP  

作　　者：Cheng-cheng Yang Dan Meng Kan Zhan Yu-lu Chen Hui Zhang Min Wu 倪恨美 

机构地区：[1]School of Chemistry and Chemical Engineering,Southeast University

出　　处：《Chinese Journal of Polymer Science》2014年第4期476-487,共12页高分子科学（英文版）

基　　金：financially supported by the National Natural Science Foundation of China(No.51073035);the International Corporation Project(No.201101088)with Science and Technology Bureau,Nanjing Municipal

摘　　要：ATRP-template dispersion polymerization of methacrylic acid （MAA） on the template of polyvinyl pyrrolidone （PVP K-30） was carried out in the aqueous solution by using methyl 2-bromopropionate （MBP）/CuC1/2,2＇-bipyridine （bpy） as the initiation system. The scanning electron microscopy （SEM）, dynamic light scattering （DLS） and gel permeation chromatography （GPC） were employed for evaluating the results of polymerization. As a result, the minimonomer droplets formed due to the H-bond interaction of PVP-MAA. The stability of droplets was dependent on pH and the concentrations of both PVP and MAA. When pH 〈 2, the coagulum of PVP-MAA formed, whereas when pH 〉 4.5, the droplets were not observable by DLS. In order to prepare the stable latex, the concentration of PVP should be lower than 9 wt%, whilst the concentration of MAA should be lower than 5.5 wt%. The optimum condition was pH 2.4, PVP 4.76 wt% and MAA 5 wt%, by which the stable latex of ca. 50 nm nanoparticles of PMAA/PVP was prepared by ATRP polymerization and simultaneously the molar mass of PVP was duplicated by PMAA according to GPC diagrams. In contrast, by using AIBN, KPS and KPS-Na2SO3 redox initiation system, the coagulum accompanying with the larger molar mass of PMAA was obtained, irrespective of pH and concentrations of PVP and MAA.ATRP-template dispersion polymerization of methacrylic acid （MAA） on the template of polyvinyl pyrrolidone （PVP K-30） was carried out in the aqueous solution by using methyl 2-bromopropionate （MBP）/CuC1/2,2＇-bipyridine （bpy） as the initiation system. The scanning electron microscopy （SEM）, dynamic light scattering （DLS） and gel permeation chromatography （GPC） were employed for evaluating the results of polymerization. As a result, the minimonomer droplets formed due to the H-bond interaction of PVP-MAA. The stability of droplets was dependent on pH and the concentrations of both PVP and MAA. When pH 〈 2, the coagulum of PVP-MAA formed, whereas when pH 〉 4.5, the droplets were not observable by DLS. In order to prepare the stable latex, the concentration of PVP should be lower than 9 wt%, whilst the concentration of MAA should be lower than 5.5 wt%. The optimum condition was pH 2.4, PVP 4.76 wt% and MAA 5 wt%, by which the stable latex of ca. 50 nm nanoparticles of PMAA/PVP was prepared by ATRP polymerization and simultaneously the molar mass of PVP was duplicated by PMAA according to GPC diagrams. In contrast, by using AIBN, KPS and KPS-Na2SO3 redox initiation system, the coagulum accompanying with the larger molar mass of PMAA was obtained, irrespective of pH and concentrations of PVP and MAA.

关 键 词：Nanoparticle ATRP Dispersion polymerization Template polymerization Hydrogel. 

分 类 号：O631.5[理学—高分子化学] O632.51[理学—化学]