化学刻蚀铝箔集流体在超级电容器中的应用  

Application of chemical etched aluminum foil collector in supercapacitor

作　　者：何捍卫[1] 周海生[1] 潘登宇[1] 

机构地区：[1]中南大学粉末冶金国家重点实验室,湖南长沙410083

出　　处：《电池》2014年第1期31-33,共3页Battery Bimonthly

摘　　要：比较了不同化学刻蚀时间后铝箔集流体的表观形貌和比表面积，用交流阻抗、恒流充放电和循环伏安等测试分析了铝箔制备的电极的性能。随着铝箔刻蚀时间的延长与腐蚀程度的增加，电极的比电容增大、等效串联电阻减小；当刻蚀时间为80 s时，电极的比电容（165.2 F/g）最大、等效串联电阻（1.4Ω）最小；刻蚀铝箔集流体制备的电极以0.3 A/g的电流在0～2.7 V循环2000次，电容衰减率不超过1.1％。The apparent morphology and specific surface area of aluminum foil collector after chemical etched for different time were compared;the performance of electrodes prepared by aluminum foil was analyzed by A.C. impedance,galvanostatic charge-dis-charge and cyclic voltammetry. With the etching time prolonged and corrosion degree increased,the specific capacitance of the elec-trode increased,the equivalent series resistance decreased. The biggest specific capacitance of 165.2 F/g and smallest equivalent series resistance of 1.4Ωof electrode could be obtained when the etching time was 80 s. When cycled for 2 000 times with the cur-rent of 0.3 A/g in 0~2.7 V,the capacitance decay rate of electrode prepared by etched aluminum foil was less than 1.1%.

关 键 词：超级电容器 化学刻蚀 铝集流体 电化学性能 

分 类 号：TM53[电气工程—电器]