Fe_(75)Zr_3Si_(13)B_9 magnetic materials prepared by spark plasma sintering  

放电等离子烧结制备Fe_(75)Zr_3Si_(13)B_9磁性材料（英文）

作　　者：王兴华[1] 王葛[1] 朱玉英[1] 鲍金峰 杜雄飞[1] 李强 

机构地区：[1]燕山大学国家冷轧板带装备及工艺工程技术研究中心,秦皇岛066004 [2]燕山大学亚稳材料制备技术与科学国家重点实验室,秦皇岛066004 [3]河北工业大学材料科学与工程学院,天津300401

出　　处：《Transactions of Nonferrous Metals Society of China》2014年第3期712-717,共6页中国有色金属学报（英文版）

基　　金：Project(13961001D)supported by the Key Basic Research Project of Hebei Province,China;Project(2013BAE08B01)supported by the National Key Technology R&D Program of China

摘　　要：Fe75Zr3Si13B9 magnetic amorphous powders were fabricated by mechanical alloying. Bulk amorphous and nanocrystalline alloys with 20 mm in diameter and 7 mm in height were fabricated by the spark plasma sintering technology at different sintering temperatures. The phase composition, glass transition temperature （Tg）, onset crystallization temperature （Tx）, peak temperature （Tp） and super-cooled liquid region （ΔTx） of Fe75Zr3Si13B9 amorphous powders were analyzed by X-ray diffraction （XRD） and differential scanning calorimetry （DSC）. The phase transition, microstructure, mechanical properties and magnetic performance of the bulk alloys were discussed with X-ray diffractometer, scanning electron microscope （SEM）, Gleeble 3500 and vibration sample magnetometer （VSM）, respectively. It is found that with the increase in the sintering temperature at the pressure of 500 MPa, the density, compressive strength, micro-hardness and saturation magnetization of the sintering samples improved significantly, the amorphous phase began to crystallize gradually. Finally, the desirable amorphous and nanocrystalline magnetic materials at the sintering temperature of 863.15 K and the pressure of 500 MPa have a density of 6.9325 g/cm3, a compressive strength of 1140.28 MPa and a saturation magnetization of 1.28 T.采用机械合金化技术制备Fe75Zr3Si13B9非晶合金粉体,利用SPS放电等离子烧结技术在不同烧结温度下将非晶合金粉体制备成d20 mm×7 mm的块体非晶纳米晶合金。采用XRD和DSC分析了Fe75Zr3Si13B9非晶合金粉体的相组成、玻璃转变温度Tg、开始晶化温度Tx和晶化峰温度Tp。然后利用XRD、SEM、Gleeble3500、VSM分析不同烧结温度下块体的相转变、微观形貌、力学性能和磁性能。研究表明,在500 MPa的烧结压力下,随着烧结温度的升高,非晶相开始晶化形成非晶纳米晶双相结构,同时,样品的致密度、抗压强度、微观硬度、饱和磁化强度均显著提高。最后在500 MPa的烧结压力和863.15 K的烧结温度下,获得密度6.9325 g/cm3、抗压强度1140.28 MPa、饱和磁化强度1.28 T的非晶纳米晶磁性材料。

关 键 词：mechanical alloying amorphous and nanocrystalline alloys saturation magnetization spark plasma sintering 

分 类 号：TF124.5[冶金工程—粉末冶金]