Mg/C/Al储氢材料制备及其吸放氢性能研究  

Preparation and hydrogen absorption /desorption property of Mg /C /Al hydrogen storage material

作　　者：卢国俭[1] 周仕学[2] 

机构地区：[1]连云港师范高等专科学校,江苏连云港222006 [2]山东科技大学化学与环境工程学院,山东青岛266510

出　　处：《现代化工》2014年第4期105-107,109,共4页Modern Chemical Industry

基　　金：国家自然科学基金项目(21176145)

摘　　要：将镁粉、微晶碳、铝粉反应球磨制备70Mg30CxAl系列储氢材料,XRD测试表明,复合材料主相为MgH2、Mg和Al,纳米晶粒在16.5 ～73.4 nm之间.随着Al质量分数的增加,材料的活化能降低显著,放氢速率增加明显,但储氢密度有所降低.在低温区放氢,Al质量分数越高,放氢量越大,放氢时间越短.70Mg30CxAl-based hydrogen storage materials are prepared by reactive milling of magnesium,crystalline carbon and aluminum.XRD analysis shows that the diffraction peaks of MgH2,Mg and Al are apparent,and the crystallite size is 16.5-73.4 nm.Increasing the amount of aluminum,the activation energy of the material decreases and hydrogen desorption rate increases obviously,but the hydrogen capacity decreases.The material would release more hydrogen at a lower temperature in a shorter time when adding more Al.

关 键 词：镁 铝 吸放氢 活化能 

分 类 号：TG139[一般工业技术—材料科学与工程]