WC含量对Ni-WC复合镀层摩擦磨损性能的影响  

Effect of WC Concentration on Wear Resistance of Ni-WC Composite Coating

作　　者：孙万昌[1] 侯冠群[1] 丁晋[1] 张磊 佘晓林 

机构地区：[1]西安科技大学材料学院,陕西西安710054 [2]中国船舶重工集团第十二研究所,陕西兴平713102

出　　处：《热加工工艺》2014年第10期151-154,共4页Hot Working Technology

基　　金：国家自然科学基金资助项目(50172023);陕西省教育厅专项计划资助(11JK0824);榆林市产学研科技计划项目(2012)

摘　　要：采用复合电沉积技术在45钢基体表面制备了Ni-WC复合镀层,利用扫描电镜、X射线衍射以及能谱分析对复合镀层的截面形貌及相结构进行了观察分析,探讨了镀液中WC颗粒含量对镀层显微硬度及摩擦磨损性能的影响。结果表明,WC颗粒均匀地分散于镀层中并由Ni基质包覆,镀层与基体结合良好,镀态下镀层为晶态结构。当镀液中WC颗粒含量为25g/L时,镀层的显微硬度、摩擦磨损性能均达到最佳。Ni-WC composite coatings were prepared on medium carbon steel 45 by composite electrodeposition method. The morphologies and phases of Ni-WC composite coating were studied by SEM, EDS and XRD. The influences of WC concentration in bath on micro-hardness and wear resistance of the composite coating were investigated. The results indicate that WC particles are uniformly distributed in the coating, Ni-WC composite coating showes a good adhesion to the substrate. And the structure of Ni matrix is crystalline. Ni-WC composite coating with 25 g/L WC particles in bath exhibites a maximal micro-hardness and wear resistance.

关 键 词：复合电沉积 Ni-WC复合镀层 显微硬度 摩擦磨损性能 

分 类 号：TG174.44[金属学及工艺—金属表面处理]