7050铝合金热压缩动态再结晶研究  

Dynamic recrystallization of 7050 aluminium alloy by hot compression

作　　者：张月婷[1] 贾耀军[1] 肖红[1] 周杰[1] 高林 

机构地区：[1]重庆大学材料科学与工程学院,重庆400044 [2]中国第二重型机械集团公司,四川德阳618013

出　　处：《兵器材料科学与工程》2014年第3期52-54,共3页Ordnance Material Science and Engineering

基　　金：国家自然科学基金面上项目(51275543);国家科技部重大专项项目(2012ZX04010-081);重庆大学大型仪器设备开放基金(2012121516)

摘　　要：用Gleeble-1500D热模拟压缩试验对7050铝合金高温流变和动态再结晶行为进行研究。结果表明:综合考虑温度和应变速率对动态再结晶的影响,得到动态再结晶峰值应变方程εp=0.015427×ε0.06081·exp(15319/RT),峰值应变与临界应变的关系εc=0.72εp,从而为有限元数值模拟和热加工工艺提供理论和数据参考。The hot deformation behavior and dynamic recrystallization of 7050 aluminum alloy were investigated on Glee- ble-1500D thermal/mechanical simulator. The results show that the peak strain equation of dynamic recrystallization is εp=0.015 427×ε 0.060 81 exp（15 319/RT）. exp（15 319/RT）with the consideration of temperature and stress rate, and the relation between peak strain and critical strain is εc=0.72εp , which provides the theoretical and data reference for finite element analysis and thermal processing.

关 键 词：铝合金 热压缩 动态再结晶 临界应变 

分 类 号：TG146.2[一般工业技术—材料科学与工程]